Hybrid contact lens system and method

ABSTRACT

A hybrid contact lens comprises a central zone comprising a substantially rigid, gas permeable material having a DK of at least 30, a relatively soft peripheral zone and an intermediate zone comprising a film or coating that is created around the central zone, and then cured. The film facilitates chemical bonding between the central zone and the peripheral zone, and also provides a protective barrier to prevent modification of the physical characteristics of the central zone. The film may be created by soaking the central zone in a chemical solution for a predetermined amount of soaking time.

FIELD OF THE INVENTION

The present invention generally relates to hybrid contact lenses, andmore particularly to hybrid hard-soft contact lenses including a gaspermeable central zone having a DK value of at least 30, an intermediatezone comprising a film or coating, and a relatively soft peripheralzone.

BACKGROUND OF THE INVENTION

Vision correction is on the verge of a revolution. New technologies tomeasure the aberrations or distortions in the optics of the eye willsoon be available to the public. These new wavefront measurementtechniques such as Shack-Hartmann wavefront sensing or TalbotInterferometry can precisely measure the eye's aberrations so thatvision may be corrected up to 20/10. Wavefront sensing is the method forrapidly, and very accurately, assessing the aberrations in anindividual's eye to create a customized prescription for correction.

However, once the eye's aberrations have been measured, either byconventional methods or by wavefront sensing, these measurements mustthen be transferred into a vision correction system, such as eyesurgery, spectacles, or contact lenses. Recent advances in laserrefractive surgery techniques such as LASIK and photorefractivekeratectomy, as well as improvements in spectacle lens manufacturing nowenable the creation of highly accurate corrective prescriptions forindividuals.

However, this is not the case with contact lenses. Popular soft contactlenses cannot achieve the same result as spectacles or laser refractivesurgery because of dimensional variations in fabrication. Hard contactlenses, which may provide the platform to achieve the results ofspectacles, are not as comfortable as soft contacts and lack thenecessary positional stability on the eye.

Hybrid hard-soft contact lenses comprising a hard center portion and arelatively soft outer skirt have been developed to provide a platformfor a corrective prescription and also provide the comfort of softcontact lenses. One drawback associate with such hybrid hard-softcontact lenses concerns a lack of a smooth transition between the softand hard portions. Another drawback involves a lack of bonding strengthbetween the soft and hard portions.

Accordingly, there exists a need for a hybrid contact lens having ajunction that provides a smooth transition between the soft and hardportions as well as sufficient bonding strength between the soft andhard portions for an improved surface. There also exists a need formethods of manufacturing such a lens.

Contact lenses that exhibit high oxygen permeability are generallypreferred for the health and comfort of the eye. However, high and hyperDK materials (e.g., materials having a DK value of at least 30) thatexhibit the requisite oxygen permeability are notoriously difficultmaterials to bond with the soft peripheral materials found in mosthybrid contact lenses. Further, the rigid center material is highlysensitive such that the penetration of soft peripheral materials andother chemical solutions into the hard center portion will alter thephysical characteristics of the sensitive high DK center portion.

Accordingly, there exists a need for a hybrid contact lens having a highor hyper DK center portion that includes a smooth transition between thesoft and hard portions as well as sufficient bonding strength betweenthe soft and hard portions for an improved surface. There also exists aneed for methods of manufacturing such a lens.

Astigmatism is a defect of the eye in which rays of light entering theeye fail to meet in a correct focal point after passing through theoptical system, thereby resulting in a blurred and imperfect image. Thedefect is usually the result of a mis-shaped or toric cornea, and thecorrection of astigmatism may be accomplished through the use of a toriccontact lens. Hybrid hard/soft contact lenses are also difficult tomanufacture since the hard and soft materials are not easily bonded toproduce a lens with acceptable boundaries. Further, the known techniquesfor making hybrid lenses are not adaptable to the manufacture of amolded lens.

Accordingly, there exists a need for a toric hybrid contact lens havinga junction that provides a smooth transition between the soft and hardportions as well as sufficient bonding strength between the soft andhard portions for an improved surface. There also exists a need formethods of manufacturing such a lens.

SUMMARY OF THE INVENTION

The present invention provides hybrid hard-soft contact lenses andmethods of manufacturing the same. Some embodiments of the inventioninclude methods of coupling the hard section of the lens (Core) to thesoft section of the lens (Skirt). Other embodiments of the inventioninclude contact lens materials that increase oxygen transmission thoughthe lens. Further embodiments of the invention are directed tocost-effective manufacturing methods of a hybrid hard-soft contact lens.

One aspect of the present invention involves a method of manufacturing ahybrid contact lens having a substantially rigid center portion and asubstantially flexible outer portion. According to a preferredembodiment, the method comprising the steps of forming the substantiallyrigid center portion, treating the substantially rigid center portion toform a coating on the perimeter of the substantially rigid portion,forming the substantially flexible outer portion around thesubstantially rigid center portion and chemically bonding thesubstantially flexible portion to the substantially rigid portion.According to some embodiments, the step of forming the substantiallyrigid center portion comprises machining a rod of substantially rigid,gas permeable, high (or hyper) DK material into a primary blank.According to other embodiments, the step of forming the substantiallyrigid center portion comprises machining the substantially rigid centerportion to form a V-shaped interface between the substantially rigid andsubstantially flexible materials.

Preferably, the step of treating the substantially rigid portion to forma coating comprises soaking the substantially rigid portion in achemical solution containing methacrylate/acrylate monomers includingmethyl methacrylate, ethyl methacrylate, butyl methacrylate orhexylmethacrylate for a predetermined amount of time. A catalyst such asa UV activator may also be employed to promote the creation of thecoating. Advantageously, the coating: (1) slows the penetration ofchemical solution into substantially rigid portion; (2) facilitateschemical bonding between the substantially rigid center portion and thesubstantially flexible outer portion; and (3) prevents changing of thephysical characteristics of the substantially rigid center portion.

According to some embodiments, the coating may be treated to promotechemical bonding between the rigid center portion and the substantiallyflexible outer portion to extend lens service life. Treating the coatingmay entail softening the coating by soaking the substantially rigidportion in a chemical solution containing methyacrylate or acrylatemonomers with an adhesion promoter and a UV activator for apredetermined amount of time. The method may further involve treatingthe surface with a mixture of the chemicals with an adhesion promoter. Afurther step involves spinning the substantially rigid portion to createa thin layer coating and to remove excess chemical solution. The step offorming the substantially flexible outer portion preferably comprisespouring liquefied substantially flexible material around thesubstantially coated rigid center portion and curing the substantiallyflexible material, wherein the amount of time between pouring and curingis less than 1 minute. This curing step may involve the use of heat, UVcuring, or combination of both. According to some embodiments, anadditional step involves increasing the viscosity of the HEMA basedresin by adding a predetermined amount of UV initiator and exposing itto a predetermined amount and duration of UV energy under continuousagitation. The pre-polymerized resin has minimized shrinkage and higherviscosity prevents the resin from penetrating the rigid center andmodifying its physical characteristics.

Any of the hybrid contact lenses of the present invention may be lathedto produce a toric lens for the correction of astigmatism.Advantageously, the shape of a toric lens permits a tear layer to beformed between the lens and the cornea, thereby improving the comfortand health of the eye. The base curve of the high or hyper DK center ofthe lens preferably is machined to approximate the shape of the lenswearer's cornea such that the radius of curvature of the soft peripheralskirt is greater than the base curve of the high or hyper DK gaspermeable center. The tear layer entrapped between the lens and thecornea serves as a refracting medium having the shape defined by thebase curve, thereby correcting the astigmatic error of the mis-shapedcornea below. At the same time, the softer, thinner peripheral portionof the lens conforms to the cornea and supports the optical zone inposition, resulting in greater comfort for the wearer.

An aspect of the present invention involves a hybrid contact lens havinga central zone, a peripheral zone and an intermediate zone comprising afilm that is created around the central zone and cured. Advantageously,the film: (1) facilitates chemical bonding between the central zone andthe peripheral zone; and (2) prevents modification of the physicalcharacteristics of the central zone. According to some embodiments, thefilm is created by soaking the central zone in a chemical solution for apredetermined amount of soaking time. The chemical solution preferablycontains one or more acrylates, such as methyl methacrylate, ethylmethacrylate, butyl methacrylate and hexylmethacrylate. The central zonepreferably comprises a substantially rigid, gas permeable material thatis a high DK material having a DK value between about 30 and about 250.According to some embodiments, the substantially rigid, gas permeablematerial is a hyper DK material having a DK value of at least 250.

Another aspect of the present invention involves a hybrid contact lenshaving a central zone, a peripheral zone and an intermediate zonecomprising one or more acrylates such as methyl methacrylate. Theintermediate zone preferably is a film that is formed around the centralzone by soaking the central zone in a chemical solution for apredetermined amount of soaking time and then curing. According to someembodiments, the intermediate zone forms a curvilinear junction betweenthe central and peripheral zones.

A further aspect of the present invention involves a hybrid contact lenshaving a substantially rigid center portion having a DK value greaterthan 30, a substantially soft peripheral portion and an intermediateportion disposed between the hard and soft portions. The intermediateportion may comprise one or more oligomer acrylate monomers as well asan adhesion promoter. The adhesion promoter may be selected from thegroup consisting of epoxy acrylates, urethane acrylates, carboxylic acidhalf esters, polyester acrylates, acrylated acrylics and low viscositymonomers.

An additional aspect of the present invention involves a hybrid contactlens having a center portion comprising a first material, a peripheralportion comprising a second material and an intermediate portioncomprising a third material, wherein each of the first, second and thirdmaterials have different compositions. Similar to previous embodiments,the center portion preferably comprises a substantially rigid, gaspermeable material having a DK value of at least 30, for examplefluorosiloxane acrylate, methyl methacrylate, ethyl methacrylate,butylmethacrylate and/or hexylmethacrylate

Yet another aspect of the present invention involves a hybrid contactlens having a central zone, a peripheral zone and a curvilinearintermediate zone comprising a convex surface that faces the peripheralzone and a concave surface that faces the central zone. Such a contactlens includes a transition area comprising the curvilinear intermediatezone and a portion of the central and peripheral zones. The radius ofcurvature of the curvilinear intermediate zone preferably is selected toreduce the amount of peripheral zone material within the transitionarea. According to some embodiments, the radius of curvature of thecurvilinear intermediate zone is selected such that the percentage ofperipheral zone material within the transition area preferably is lessthan about 30 percent, most preferably less than about 20 percent.Advantageously, the curvilinear intermediate zone improves bondingstrength between the central and peripheral zones, thereby reducing theincidence of lens failure.

A further aspect of the present invention involves a toric hybridcontact lens having a central zone, a peripheral zone and anintermediate zone, wherein the central zone comprises a substantiallyrigid, gas permeable material having a DK of at least 30. The centralzone preferably is machined to approximate the shape of a lens wearer'scornea such that the radius of curvature of the peripheral zone isgreater than that of the central zone. Such a toric hybrid contact lensis dimensioned to correct the astigmatic error of a lens wearer'scornea.

An additional aspect of the present invention involves a method offorming a hybrid contact lens, including the steps of forming a centralzone, forming a protective barrier around the central zone andchemically bonding a peripheral zone to the central zone.Advantageously, the protective barrier: (1) facilitates subsequentchemical bonding between the central and peripheral zones; and (2)prevents modification of the physical characteristics of the centralzone. The central zone preferably comprises a substantially rigid, gaspermeable material that is a high DK material having a DK value betweenabout 30 and about 250. According to some embodiments, the substantiallyrigid, gas permeable material is a hyper DK material having a DK valueof at least 250.

Another aspect of the present invention involves a hybrid contact lenshaving a central zone, a first intermediate zone, a second intermediatezone and a peripheral zone. The first intermediate zone is a film thatis created around the central zone and cured, whereas the secondintermediate zone is a film that is created around the firstintermediate zone and cured. Advantageously, the first and secondintermediate zones facilitate chemical bonding between the central zoneand the peripheral zone, and also prevent modification of the physicalcharacteristics of the central zone. The central zone preferablycomprises a substantially rigid, gas permeable material having a DK ofat least 30.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a front view of a manufacturing step used to construct ahybrid hard-soft contact lens of the present invention;

FIG. 2 is a front view of a contact lens blank after the manufacturingstep illustrated in FIG. 1;

FIG. 3 is a front view of another manufacturing step used to construct ahybrid hard-soft contact lens of the present invention;

FIG. 4 illustrates another manufacturing step used to construct a hybridhard-soft contact lens of the present invention;

FIG. 5 illustrates an alternative manufacturing method of constructing ahybrid hard-soft contact lens of the present invention;

FIG. 6 illustrates several embodiments of interface geometries between ahard section and soft section of a hybrid hard-soft contact lensconstructed according to the present invention;

FIG. 6A illustrates a preferred embodiment of an interface geometrybetween a hard section and soft section of a hybrid hard-soft contactlens constructed according to the present invention;

FIG. 7 is an illustration of a contact lens, several eye components andvisible light rays exiting the eye-contact lens system;

FIG. 8 is another illustration of a contact lens, eye components andvisible light rays, showing the tendency for different colored lightrays to exit the eye at different angles;

FIG. 9 illustrates a hypothetical uniform eye response to the visiblelight spectrum;

FIG. 10 illustrates a photopic eye response to the visible lightspectrum; and

FIG. 11 illustrates one idealized net wavelength response for a contactlens constructed according to the present invention.

FIG. 12 is a cross-sectional view of a hybrid contact lens moldaccording to the principles of the present invention;

FIGS. 13A-13D are cross-sectional views of the hybrid contact lens moldsof FIG. 12, wherein each view includes an alternative inner wall;

FIG. 14 is a cross-sectional view of the hybrid contact lens mold ofFIG. 12 after the inner section has been filled with a substantiallyrigid polymer and cured;

FIG. 15 is a cross-sectional view of the hybrid contact lens mold ofFIG. 14 after the outer section has been filled with a substantiallyflexible polymer and cured;

FIG. 16 is a cross-sectional view of an alternative hybrid contact lensmold according to the principles of the present invention;

FIGS. 17A-17D are cross-sectional views of the hybrid contact lens moldsof FIG. 16, wherein each view includes an alternative junction shape;

FIG. 18 is a cross-sectional view of the hybrid contact lens mold ofFIG. 16 after the central void is filled with a substantially rigidpolymer and cured;

FIG. 19 is a cross-sectional view of the hybrid contact lens mold ofFIG. 18 after separation of the mold;

FIG. 20 is a cross-sectional view of the hybrid contact lens mold ofFIG. 19 after the addition of a guard;

FIG. 21 is a cross-sectional view of the hybrid contact lens mold ofFIG. 20 after the substantially flexible polymer is poured and cured;

FIG. 22 is a cross-sectional view of a further alternative hybridcontact lens mold according to the principles of the present invention;

FIG. 23 is a cross-sectional view of the hybrid contact lens mold ofFIG. 22 after the inner section has been filled with a substantiallyrigid polymer and cured;

FIG. 24 is a cross-sectional view of the hybrid contact lens mold ofFIG. 23 after the outer has been filled with a substantially flexiblepolymer and cured;

FIG. 25 is a cross-sectional view of another alternative hybrid contactlens mold according to the principles of the present invention;

FIG. 26 is a cross-sectional view of the hybrid contact lens mold ofFIG. 25 after the central void has been filled with a substantiallyrigid polymer and cured;

FIG. 27 is a cross-sectional view of the hybrid contact lens mold ofFIG. 26 after separation of the mold;

FIG. 28 is a cross-sectional view of the hybrid contact lens mold ofFIG. 27 after the addition of a guard;

FIG. 29 is a cross-sectional view of the hybrid contact lens mold ofFIG. 28 after the substantially flexible polymer is poured and cured;

FIG. 30 is a cross-sectional view of a pre-formed substantially rigidcenter portion suitable for use with the pre-shape mold of FIGS. 31-33;

FIG. 31 is a cross-sectional view of yet another alternative hybridcontact lens mold according to the principles of the present invention;

FIG. 32 is a cross-sectional view of the hybrid contact lens mold ofFIG. 31 after the outer portion of the bowl-shaped void has been filledwith a substantially flexible polymer and cured; and

FIG. 33 is a cross-sectional view of the hybrid contact lens mold ofFIG. 32 after separation of the mold.

FIG. 34 is a cross-sectional view of a primary blank of substantiallyrigid material used in connection with a method of manufacturing ahybrid contact lens according to the principles of the presentinvention;

FIG. 35 is a cross-sectional view of the primary blank of substantiallyrigid material of FIG. 34 disposed within a cup;

FIG. 36 is a cross-sectional view of the primary blank of substantiallyrigid material of FIG. 34 soaking in a chemical solution within the cup;

FIG. 37 is a cross-sectional view of a coating formed on the primaryblank of substantially rigid material of FIG. 34;

FIG. 38 is a cross-sectional view of the primary blank of substantiallyrigid material of FIG. 37 soaking in a chemical solution within the cup;

FIG. 39 is a cross-sectional view of the primary blank of substantiallyrigid material of FIG. 37 soaking in another chemical solution withinthe cup;

FIG. 40 is a cross-sectional view of the primary blank of substantiallyrigid material of FIG. 37 after liquefied substantially flexiblematerial has been poured and cured;

FIG. 41 is a cross-sectional view of a hybrid contact lens produced bythe method of manufacturing a hybrid contact lens of FIGS. 34-40; and

FIG. 42 is an enlarged cross-sectional view of the junction betweensubstantially flexible and substantially rigid materials of the hybridcontact lens of FIG. 41.

FIG. 43 is a cross-sectional view of a hybrid contact lens having acentral zone, an intermediate zone and a peripheral zone;

FIG. 44 is an enlarged cross-sectional view of the intermediate zone ofthe hybrid contact lens of FIG. 43;

FIG. 45 is a cross-sectional view of a hybrid contact lens having acentral zone, a curvilinear intermediate zone and a peripheral zone;

FIG. 46 is an enlarged cross-sectional view of the curvilinearintermediate zone of the hybrid contact lens of FIG. 45;

FIG. 47 is a cross-sectional view of a hybrid contact lens having acentral zone, a first intermediate zone, a second intermediate zone anda peripheral zone; and

FIG. 48 is an enlarged cross-sectional view of the first and secondintermediate zones of the hybrid contact lens of FIG. 47.

It will be recognized that some or all of the Figures are schematicrepresentations for purposes of illustration and do not necessarilydepict the actual relative sizes or locations of the elements shown.

DETAILED DESCRIPTION OF THE INVENTION

In the following paragraphs, the present invention will be described indetail by way of example with reference to the attached drawings.Throughout this description, the preferred embodiment and examples shownshould be considered as exemplars, rather than as limitations on thepresent invention. As used herein, the “present invention” refers to anyone of the embodiments of the invention described herein, and anyequivalents. Furthermore, reference to various feature(s) of the“present invention” throughout this document does not mean that allclaimed embodiments or methods must include the referenced feature(s).

The present invention is based on a hybrid contact lens platform thatoffers the benefits, without the disadvantages, of both soft and gaspermeable contact lenses comfort, health, stability, superior optics anddurability. The features of the present invention include lenschemistry, manufacturing processes, optical design and prescribing andfitting processes. One feature of the manufacturing processes andoptical design elements is the ability to make quarter wavelengthcustomization in order to correct for the higher order refractiveaberrations that limit one's ability to see better than 20/20.

Unless defined otherwise, all technical and scientific terms used hereinhave the same meaning as is commonly understood by one of skill in theart to which this invention belongs. In event the definition herein isnot consistent with definitions elsewhere, the definitions set forthherein will control. As used herein, “hybrid” refers to a type ofcontact lens that includes both hard and soft lens elements whichchemically bonded or stitched together.

One embodiment of the present invention will correct normal ametropicerrors (myopia, hyperopia and astigmatism) to a higher degree of visualperformance than conventional contact lenses. Another embodiment of thepresent invention will correct for the wavefront-guided higher orderaberrations and will create a new contact lens category, providing“super vision” for those whose visual requirements demand better than20/20 acuity. Yet another embodiment of the present invention willcorrect for presbyopia, the gradually increasing inability to focus atclose distances that usually begins after age 40. Other embodiments ofthe present invention may include contact lenses that incorporateseveral, or all of the above-described features.

Another embodiment of the present invention is a hybrid lens thatcombines the optical clarity, stability and durability of a gaspermeable lens with the comfort of a soft contact lens. This hybrid lenshas a high or hyper DK gas permeable center chemically bonded to awettable soft outer skirt. The center is highly oxygen permeable, whichis important to maintaining corneal health. One of the manufacturingprocesses of the present invention enables this gas permeable center tobe lathed to quarter wavelength precision, allowing corrections ofwavefront-guided higher order refractive aberrations and providingvisual performance better than 20/20.

Yet another embodiment hybrid contact lens of the present inventioninvolves a toric lens having a soft outer skirt with a radius ofcurvature greater than the base curve of the oxygen permeable center,which is suspended on the soft skirt, thus creating a lighter touchabove the corneal apex. One feature of this embodiment is that theeyelid force of normal blinking creates a peristaltic-like pump thatexchanges the tears under the lens, contributing to overall comfort, andeliminating dryness, the most frequent complaint of contact lenswearers. Another feature of this embodiment is that the tear layer underthe lens is not only important for comfort and health, but it also hasoptical correction qualities as well. A layer of tears retained behindthe base curve of the gas permeable lens of the present invention maycorrect corneal astigmatism by up to about ten diopters. Thus, a hybridcontact lens constructed according to the present invention creates asuperior astigmatism correcting capability that does not rely onorientation and positioning, as do soft contact lenses.

Another embodiment of the present invention comprises a hybrid lens witha substantially rigid center that is chemically bonded to a softer outerskirt. One embodiment of the outer skirt is comprised of a modifiedpoly(2-hydroxyethyl methacrylate) HEMA(poly-2-hydroxyethylmethacrylate), methacrylate monomer (C1 to C6)materials including perfluorinated methacrylate, siliconatedmethacrylate, and a crosslinking agent. The center is a substantiallyrigid gas permeable-type with a gas permeability DK value greater than30, preferably about 150. However, other embodiments may have a gaspermeability DK value that may range about 30 to greater than 250.Suitable materials for the substantially rigid center includefluoro-siloxane acrylate, siloxane acrylate, and poly-stryene siloxaneacrylate.

The substantially rigid center section may have a thickness that mayrange between about 0.03 millimeters (mm) to about 0.5 mm., and adiameter that may range between about 4.0 mm. to about 12.0 mm. Theoverall diameter of a hybrid contact lens constructed according to thepresent invention may range between about 10.0 mm. to about 18.0 mm.

The substantially rigid center may have a spherical or ellipsoidalocular (i.e., eye-facing) surface. Unlike soft lenses, the substantiallyrigid center of the present invention contact lens is resistant toprotein deposition. One feature of the present invention contact lens isthat it is also highly resistant to foreign body migration as well asdislodgement from the eye during contact sports, or other vigorousactivities. A contact lens constructed according to the presentinvention also provides excellent centering and vision correction forirregular corneas created by trauma or surgery.

Hybrid Contact Lens Geometry

One embodiment of the present invention comprises a centralsubstantially rigid gas permeable portion having a posterior surfacethat is either spherical, aspherical or toroidal, which is chosen toapproximate the overall toricity and sagittal depth of the cornea to befitted. The rigid gas permeable portion may be optically clear with onlythe reduction in light transmission normally found in similarpolymerized materials. In one embodiment the rigid portion containscolorants and additives that narrow the band of light transmitted by thelens to reduce the chromatic aberration of the lens-eye system. Theanterior or posterior surface of the rigid portion may also have surfacemodification to correct the total low and high order aberrations of thelens-eye system. Further, the surface profile of the anterior orposterior surface may be modified to register the low and high orderaberrations over the optical system of the eye to account for theconsistent natural displacement of the contact lens when applied to theeye. In addition, the surface profile of the anterior or posteriorsurface may be modified to contain a multi-focal feature for thecorrection of presbyopia. Also, the anterior surface of the lens may betreated to reduce the variance in the pre-lens tear film.

In another embodiment of the present invention, the substantially rigidcontact lens portion is joined to an outer soft hydrophilic portion byan intermediate adhesion enhancement zone. The adhesion enhancement zonemay contain a material that bonds to the substantially rigid portion andto the soft hydrophilic portion. The soft hydrophilic portion may have aposterior surface that is spherical, aspherical, toroidal orrotationally asymmetrical to approximate the overall or meridionalsagittal depth of the peripheral cornea, limbal region and sclera. Theanterior surface of the soft portion may be modified to produce athickness variation in the form of prism ballast or thin zones thatutilize lid interaction to produce a resultant rotational stability.

The soft section or skirt of the contact lens is designed to controlrotation by various methods. The methods include prism ballasting, thinzones, and rotationally asymmetrical contours that match the asymmetryof the cornea, limbus and sclera. According to some embodiments, thesuperior portion of the lens is thinner than the inferior portion.

Methods of Manufacturing a Hybrid Contact Lens

Referring to FIGS. 1-5, one method of manufacturing a hybrid contactlens according to the present invention will now be described. Thismethod results in a fracture resistant product that is inexpensive tomanufacture.

Shown in FIG. 1, a rod 10 of substantially rigid, gas permeable, high(or hyper) DK material is cast having the desired characteristics. Uponthe completion of the curing the rod is precision ground to produce asubstantially uniform diameter. The rod is then machined by tool 15 intoa primary blank 17 having an anterior diameter 20 designed to conform tothe collet of a computer numerically controlled lathe and a posteriordiameter 25 designed to conform the outermost diameter of thehydrophilic portion of the lens for positioning in a tube, cup, or othercontaining device. The anterior diameter 20 may range from 6 millimeters(mm) to 24 mm, and the posterior diameter 25 may range from 6 mm to 24mm. In one embodiment, the anterior diameter 20 may be a separatematerial that is bonded or otherwise attached to the primary blank 17for enduring the clamping force of a lathe. The intermediate portion ofthe primary blank 17 is simultaneously machined to have a predeterminedangle 30 for the interface of the rigid and hydrophilic material in thefinished lens.

One manufacturing method of the present invention has the posteriordiameter 25 substantially meet, or exceed, the hydrophilic sectionoutermost diameter 35, that is, the outermost diameter of the softsection of the contact lens, as shown in FIG. 4. In this embodiment, aboundary material 40 is then applied to produce a resultant wall, or cupto receive, and retain the hydrophilic liquid polymer. Alternatively,the primary blank 17 may be inserted into a cup, tube or othercontaining device to receive the hydrophilic material.

An alternative manufacturing method of the present invention includesthe application of an adhesion promoter to the primary blank 17,followed by the casting of the hydrophilic polymer into the liquidholding device formed by the boundary material 40, tube, cup or othercontaining device.

In yet another embodiment, the primary lens blank 17 is mounted via theanterior diameter 20 in the collet of a computer numerically controlledlathe that is programmed to produce the aspherical posterior surfaceprofile in a manner that the profile does not require polishing, or mayonly need a light buff, or polish. The posterior surfaced button is thenmounted to a lens block wherein the axis of the block passes through thegeometric center of the lens 45, shown in FIG. 4.

The assembly with the posterior surfaced button is remounted in thecollet of a computer numerically controlled lathe, such as the Optoform80 with Variform attachment, or equivalent type that is capable ofproducing rotationally symmetrical or non-symmetrical surfaces to high,or quarter wavelength accuracy that preferably require a light buff, orno supplemental polishing (VARIFORM and OPTOFORM are trademarks ofPrecitech, Inc., of Keene, N.H.). It will be appreciated to thoseskilled in the art that other types of lathes may be employed. Thefinished lens is then removed from the lathe, with or without a lightbuff, deblocked and cleaned followed by anterior lens surface treatment.Finally the lens undergoes hydration-extraction, sterilization andpackaging.

Alternative manufacturing methods of the present invention may include:molding of the posterior surface and diamond turning of the moldedblank; contour cutting of the anterior surface of a posterior curvefinished blank; etching the anterior surface of a posterior curvefinished blank or predicate lens anterior or posterior surface; thinfilm deposition of a predicate lens anterior or posterior surface; andlaser ablation of a predicate lens anterior or posterior surface.

Another manufacturing method may include molding or lathing a standardbase curve with a standard or semi-customized front surface, then usinga thermal or laser energy to modify the refractive index of the centermaterial to a desired optical requirement. This method replaces customlathing or molding expenses. Another method may include molding theposterior and anterior surfaces, and yet another embodiment may includea mechanical force or thermal molding manufacturing method.

Another method of manufacturing a hybrid contact lens according to thepresent invention is illustrated in FIG. 5. Step 1 shows a rod offluorosiloxane acrylate RGP material that will comprise thesubstantially rigid section of the hybrid contact lens. It will beappreciated to those skilled in the art that other types of materialsmay be employed. These other materials may include the followingmonomers, monomer mixtures, or their derivatives: methyl methacrylate;ethyl methacrylate; butylmethacrylate, hexylmethacrylate, ethyleneglycol diacrylate; octafluoro pentyl methacrylate,tetramethyldisiloxane, ethylene glycol dimethacrylate, pentafluorophenylacrylate, 2-(trimethylsiloxyl)ethyl methacrylate,2,2-bis(2-metharyloxyphenyl) propane, N-[2-(N,N-dimethylamino)ethyl]acrylate, 2-(N,N-dimethylamino)ethyl methacryalte,2-(N,N-dimethylamino)propy acrylate, N-vinyl-2-pyrrolidone,N,N-dimthylacrylamide, acrylamide, acrylamine, 2-hydroxyethylmethacrylate, siloxane-ethylene glycol dimethacrylate, trifluoroethylmethacrylate, pentafluorostyrene, pentafluorophenyl methacrylate,pentafluorophenyl acrylate, pentafluoropropyl methacrylate, unsaturatedpolyester; p-vinyl benzylhexafluoroisopropyl ether, siliconylstyrene,siloxanyl alkylmethacrylate, and siloxanylalkylamide.

The rod, or button shown in Step 1 of FIG. 5, will preferably have a 5millimeter (mm) to 22 mm diameter and be 2 mm to 15 mm in length. In oneembodiment, the button may be bonded to another material for asubsequent operation, and as a possible cost saving. In Step 2, a plungetool is used to remove unnecessary hard material and allow a solidsection of material on one side for subsequent operations. Anothermethod may use the plunge tool to form the button assembly from Step 1,with a shape similar to FIG. 2.

In Step 3, a spacer is formed on the gripping side of the blank for thenext operation, or the blank can be bonded to a pre-form containingdevice to skip Step 4.

In Step 4, a tape, or other media that provides a retaining wall to holdthe soft material during polymerization is applied to the blank. In Step5, an adhesion promoter may be applied to the hard material and then thesoft material is poured inside the retaining wall, or other containingdevice, and allowed to cure using heat, UV, or combination of heat andUV. In Step 6, the spacer, or containing device, is removed and theblank is ready for subsequent manufacturing operations.

Referring to FIG. 6, methods of coupling the hard section of the contactlens to the soft section will now be described. Conventional hybridcontact lenses are generally not durable, in part because of the weakchemical bonding between the hard and soft sections of the lens. Bondingfailure may cause cornea scratching and also cost for replacing thelens. One feature of the present invention is that a variety of couplingconfigurations are contemplated that securely couple the hard and softsections of a hybrid contact lens.

One embodiment of the present invention employs an angled, or slopedsurface between the hard and soft contact lens sections, therebyincreasing the surface area, and thus the bonding force, or strengthbetween the two sections. Other embodiments use a variety of differentsurface features, or surface geometries that increase the durability andcomfort of a hybrid contact lens.

For example, the bonding angle 50, shown in FIG. 6, may vary from almost0 degrees to almost 90 degrees. That is, if a contact lens constructedaccording to the present invention was pressed against a flat surface,the angle defined by the interface between the hard and soft sections ofthe lens could vary from almost parallel to the flat surface to almostperpendicular to the flat surface.

In addition, the interface between the hard and soft sections of thecontact lens may include a variety of surface configurations, orgeometries 55. As shown in FIG. 6, these surface geometries 55 mayinclude ledges, protuberances, or substantially V- or W-shapedprojections. Other surface geometries 55 may include serrations,gradations, or any other shape that is not substantially straight, orplanar.

Referring now to FIG. 6A, a hard-soft lens bonding method isillustrated. In this embodiment of the present invention, increasing thesurface area between the rigid and soft lens components increasesbonding strength between the two materials and minimizes lens breakage,or failure. Another advantage of this embodiment is that it provides asmooth transition between the rigid or hard, and soft materials. Thisproduces an exceptionally comfortable lens.

As shown in FIG. 6A, an interface, or junction 75 between the hard, orsubstantially rigid lens material 65, and the soft lens material 70 isillustrated. Also shown is angle “A” that may range between about 95degrees to about 170 degrees. Angle A preferably ranges between about110 degrees to about 165 degrees. As illustrated, the interface betweenthe hard, or substantially rigid lens material 65, and the soft lensmaterial 70 is substantially V-shaped. Put differently, the interfacecomprises two intersecting planes that meet within the lens. This lensjunction configuration provides a safety feature in the unlikely case oflens material separation during wear. Because of the V-shape, the edgeof the hard lens material 65 is not “blade” shaped, and thus a sharpedge will not contact the cornea or eyelid, eliminating the risk ofcuts, or abrasions.

The hard and soft sections of a contact lens constructed according tothe present invention may be joined, or coupled by a bonding material orresin comprised of the following monomer mixtures or their derivatives:vinyl acetate; trifluoroethanol; methyl methacrylate; ethylmethacrylate, butylmethacrylate, ethylene diamine; 2-hydroxyethylmethacrylate (HEMA) and other esters of methacrylic and acylic acidswith C1 to C6 carbon formulated from acrylic bases with fluorinatedalkyl or aryl, silicone, styrene moiety in the structure and resultantpolymers such as polystyrene; fluorine/styrene; and silicone/styrene.

The soft section of the contact lens constructed according to thepresent invention may be comprised of a variety of materials. Thesematerials may include: poly HEMA; hydroxyethyl acrylate; dihydroxypropylmethacrylate; butylmethacrylate, hexylmethacrylate, perfluorinatedmethacrylate esters, polyethylaneglycol; acetoxysilane;(trimethylsiloxyethyl)methacrylate; trimethylesiloxy;ethyleneglycol-dimethacrylate; phenylethyl acrylate; polyethylene oxide;and silicon hydrogels. It will be appreciated to those skilled in theart that other types of materials may be employed.

Hybrid Contact Lens Surface Treatments

One feature of the present invention is that a variety of contact lenssurface treatments are contemplated. These surface treatments may beadded, for example, for the purpose of improving the comfort of the lensby means of improving the in-vivo wetting of the lens material. Anotherreason for using surface treatments is to create a uniform pre-lens tearfilm thickness. Variations in pre-lens tear film thickness induceaberrations while a uniform pre-lens tear film thickness allows theother aberration corrections to reach full effectiveness.

One embodiment of a hybrid contact lens constructed according to thepresent invention may include a surface treatment that provides uniformpre-lens tear film thickness between normal blinking actions. Thesetreatments may comprise one or more of the following embodiments: 1)Plasma—the lens is placed in the presence of gases such as oxygen andNH₂ containing compounds, that are modified by oscillatingelectromagnetic energy. This creates a surface functionalization(oxidation) that generate functional groups such as OH or NH on the lenssurface, which make the lens surface more wettable; 2) Ionicsurfactants—polar molecules are presented to the ionic lens surfaceswith a resultant bonding of the molecules to the surface. An example issodium dodecyl sulfide. The 12-carbon chain combined with laurylsulfonic acid provides a substrate that supports a more uniform tearfilm thickness; 3) Non-ionic surfactants—The lens may be exposed tonon-ionic surfactants that provide a film on the lens. An example is anethylene glycol chain; 4) Soluable polymers—films of soluble polymerscan be applied to the rigid gas permeable material after manufacturing.Examples are, N,N-dimethyacrylamide, methacylamide, HEMA, and otherhydrophilic monomers. Other types of surface treatments are alsocontemplated.

Methods of Prescribing and Fitting a Hybrid Contact Lens

The present invention also contemplates methods of prescribing andfitting a hybrid contact lens. One method relates to non-rotating lensesfor correcting high order aberrations that include methods of placingthe coordinates of the aberration measurement over the coordinates ofthe pupil. Another comprises methods of placing a multifocal over thecoordinates of the pupil and customizing the design of the multifocalwith measurements of high order aberrations and pupil size.

One method of prescribing and fitting a hybrid contact lens employs aset of precision hybrid lenses with spherical, aspherical or toroidalposterior surfaces and spherical, aspherical or toroidal anteriorsurfaces. For a final monofocal lens, one embodiment contains aposterior aspherical surface and an anterior spherical surface. For afinal multifocal lens one embodiment contains a posterior asphericalsurface and an anterior aspherical surface.

One prescribing method of the present invention employs a centralregistration mark or marks concentric with the lens geometric centerthat are placed on either the anterior or posterior surfaces or withinthe matrix of either the rigid central portion, the intermediateadhesion enhancement zone or in the soft portion of a contact lens.According to some embodiments, the rigid portion is at least 9 mm indiameter and a minimum of three marks are placed at a chord diameter ofabout 8 mm. Additionally, the diameter of the overall lens isapproximately 14.0 mm.

A contact lens from the set with a posterior rigid surface thatapproximates the sagittal depth of the respective eye over the chorddiameter of the rigid portion is placed on the eye and allowed toequilibrate. The degree of rotational and translational movement isobserved. According to some embodiments, the movement observed should beless than 5 degrees rotational and 0.3 mm translational. Upondetermination that the movement meets the required limit the residualhigh and low order aberrations are measured through the lens along withthe relative coordinates of the lens marks and the pupil margin, limbalmargin or other anatomical features. In the preferred embodiment aninstrument having the capability of detecting the lens marks and thepupil margin along with the residual high and low order aberrations isused.

An alternative embodiment of the present invention may includeinfrared-responsive marks, such as one or more registration marks, oneor more concentric marks, or other suitable marks, which emit or reflectinfrared light. For example, some types of wavefront aberrometers employinfrared light, which is generally in the form of a laser. Duringexamination of an eye fitted with a hybrid hard-soft contact lensconstructed according to the present invention, the infrared-reflectingmarks in the hybrid lens will be easily visible, enabling simultaneousevaluation of registration error, as well as aberrations. In oneembodiment, indocyan dye that fluoresces when exposed to ultravioletlight is employed, but it will be appreciated that other dyes, powders,or other types of ultraviolet and infrared-responsive products may beemployed.

Another method of prescribing and fitting a hybrid contact lens employsa set of precision rotating and non rotating hybrid contact lenseshaving known ocular surface profiles, optical corrections and thicknessprofiles. In one embodiment, the lenses contain circumferential marks inthe mid periphery. A lens is selected and applied to the eye and allowedto equilibrate. The coordinates of the marks and the pupil aredetermined. The aberrations of the lens-eye system are measured. Amathematical model provides analysis of the known thickness profile, theregistration error of the coordinates of the lens and the pupil, and theresidual lens-eye aberrations to derive the computer numericallycontrolled lathe files for diamond turning a resultant thickness profilefor a final contact lens having the same ocular surface profile.

For example, one prescribing and fitting method of the present inventionmay include the steps of: selecting the initial lens to conform to theshape of the underlying cornea; capturing an image of thecircumferential marks and the pupil margin; measuring the residual lowand high order aberrations of the lens-eye system; performing analysisutilizing the known ocular surface profile of the lens, the initial lensthickness profile, the registration error, and the residual lens-eyeaberration error to determine the resultant files for generating a finalcontact lens.

Another method of prescribing and fitting a hybrid contact lens employsa set of contact lenses having a known central zone ocular surfacegeometry, thickness, anterior surface geometry and diameter. Thepreferred residual lens eye aberration correction and coordinatedisparity are determined by clinical measurement, and the thicknessprofile variation is derived by computer modeling, or other methods, inorder to specify a superiorly performing lens.

Yet another method of prescribing and fitting a hybrid contact lensemploys a set of contact lenses with fixed ocular surface geometries,overall diameters and front surface geometries, over which clinicalmeasurements are made from which the final prescription parameters arederived by computation, or other methods.

Another method of the present invention comprises correcting visualacuity deficiencies in presbyopia by reduction of the residual lens-eyeaberrations. The method uses a set of hybrid contact lenses having aknown ocular surface profile and thickness profile and containingcircumferential marks for the purpose of registration of the finaloptical correction with the coordinates of the optical system of theeye. The method steps may include: selecting the initial lens to conformto the shape of the underlying cornea; capturing an image of thecircumferential marks and the pupil margin; measuring the size of thepupil in photopic, mesopic and/or scotopic illumination; measuring theresidual low and high order aberrations of the lens-eye system; andperforming analysis utilizing the known ocular surface profile, theinitial lens thickness profile, the registration error, the pupil sizeand the residual lens-eye aberration error to determine prescriptioninformation for generating a final contact lens. In one embodiment ofthis method, the diameter of the near focused optical correction may bein the range of about 1.8 mm to about 4.0 mm.

Another method of the present invention employs a multifocal contactlens and corrects visual acuity deficiencies in presbyopia by reductionof the residual lens-eye aberrations. The method uses a set ofmultifocal hybrid contact lenses having a known ocular surface profileand thickness profile and containing circumferential marks for thepurpose of registration of the final optical correction with thecoordinates of the optical system of the eye. The method steps mayinclude: selecting the initial lens to conform to the shape of theunderlying cornea having a multifocal anterior surface; capturing animage of the circumferential marks and the pupil margin; measuring thesize of the pupil in photopic, mesopic and/or scotopic illumination;measuring the residual low and high order aberrations of the lens-eyesystem; and performing analysis utilizing the known ocular surfaceprofile, the initial lens thickness profile, the registration error, thepupil size and the residual lens-eye aberration error to determineprescription information for generating a final multifocal contact lens.In one embodiment of this method, the diameter of the near focusedoptical correction may be in the range of about 1.8 mm to about 4.0 mm.

Another method of the present invention employs a multifocal contactlens and corrects visual acuity deficiencies in presbyopia by reductionof the residual lens-eye aberrations. This method also incorporatesinformation relating to a light transmittance pattern. The method uses aset of multifocal hybrid contact lenses having a known ocular surfaceprofile and thickness profile, light transmittance pattern, andcontaining circumferential marks for the purpose of registration of thefinal optical correction with the coordinates of the optical system ofthe eye. The method steps may include: selecting the initial lens toconform to the shape of the underlying cornea having a multifocalanterior surface; capturing an image of the circumferential marks andthe pupil margin; measuring the size of the pupil in photopic, mesopicand/or scotopic illumination; measuring the residual low and high orderaberrations of the lens-eye system; and performing analysis utilizingthe known ocular surface profile, the initial lens thickness profile,the registration error, the light transmittance pattern, the pupil sizeand the residual lens-eye aberration error to determine prescriptioninformation for generating a final multifocal contact lens. In oneembodiment of this method, the diameter of the near focused opticalcorrection may be in the range of about 1.8 mm to about 4.0 mm.

The above-described methods of prescribing and/or fitting a hybridcontact lens may also employ additional method steps or additionaldevices. For example: the method of determining the difference in thecoordinates of the center of the circumferential lens marks and thepupil margin may incorporate a reticle of a biomicroscope or a camerawith subsequent manual or electronic digital image detection. Inaddition, the method of measuring the residual aberrations of thelens-eye system may incorporate Shack-Hartmann aberrometry, aberrometersutilizing Tscheming technology, laser ray-tracing, holographic grid orTalbot interferometry technology.

Correction for Various Components of the Visible Light Spectrum

Aberrometry performed with the contact lens in place provides us withknowledge of the angles that the rays emerging from the anterior lensmake with respect to the visual axis. In the perfect case, the rayswould all emerge parallel to the visual axis. But as illustrated in FIG.7, in the presence of aberrations these rays make an angle with respectto the visual axis and this angle is not restricted to the plane of thepaper. To correct these aberrations, there are generally two variablesto modulate. The first variable is the slope of the contact lens at thepoint each ray emerges from the contact lens. Changing this slope willchange the direction of the ray exiting the eye via Snell's Law. Therewill exist a slope of the anterior or posterior contact lens surfacethat causes the ray to exit parallel to the visual axis. The secondvariable is the local lens thickness at the point where each ray exitsthe contact lens. As this thickness is adjusted, the slope of one orboth of the surfaces for the path of the ray at this point also needs tochange in order to keep the emerging ray parallel to the visual axis.There will exist a set of local thicknesses and slopes thatsimultaneously cause all of the emerging rays to be parallel to thevisual axis and keep the overall thickness of the lens reasonable, thatis, not too thin or too thick.

Aberrometry is normally only performed at one wavelength, usually in theinfrared. However, as illustrated in FIG. 8, the slopes of the variousrays will depend on the color of the light. In general, blue lights rayswill be more convergent than the green light rays. The red light rayswill be more divergent than the green light rays.

The dilemma now is which color rays should be made parallel to thevisual axis. If the eye responded equally to all colors in the visiblerange (wavelengths of about 380 nanometers (nm) to about 780 nm), youwould make the rays that corresponded to the middle wavelength parallelto the visual axis. In this manner, half of the light would be divergingand half of the light would be converging as it left the eye.

Referring to FIG. 9, for a uniform response, the center wavelength ofthe visible spectrum would be ideal for correcting aberrations since,the equal areas of the rectangles on either side of this wavelengthmeans equal amounts of energy is distributed around this wavelength.

However, the eye does not respond to all wavelengths the same. Thephotopic response curve, illustrated in FIG. 10, shows that the eye ismore sensitive to the red/green end of the spectrum. The same sort ofconcept as described above can now be used to determine the idealwavelength for correcting aberrations. The ideal wavelength gives equalareas under the photopic response curve on either side, as shown in FIG.10.

In addition to the variation in response of the eye to different colors,the present invention may also vary the transmission of the contact lensto different colors. This may be beneficial to reducing the effects ofchromatic aberration in the eye. If the contact lens transmission ismultiplied by the photopic response of the eye, a net response of theeye results, as illustrated in FIG. 11. One ideal wavelength is based onthis net response which again gives equal areas under the curve. Thisideal wavelength is then used as the target for correcting aberrationsby the means described above.

For example, for either a final monofocal or multifocal lens, oneembodiment hybrid contact lens constructed according to the presentinvention contains colorants that reduce the transmission at both theblue and red end of the visible spectrum thereby narrowing the band oftransmitted light and potentially shifting the peak of the transmissioncurve of the lens. A contact lens of the present invention may thereforeinclude color additives for the purpose of reducing light transmission,or color additives for the purpose of reducing chromatic aberration.

An alternative example utilizes a calculation based on the knownbandwidth of a pre-existing lens material and the output of themonochromatic aberrometry measurement to determine the optimum lensthickness profile.

Methods of Manufacturing a Hybrid Contact Lens by Chemical Bonding

The present invention discloses a hybrid contact lens that providesclear vision, while featuring high gas permeability for enhanced cornealhealth and comfort. Methods of manufacturing such a hybrid contact lensare described herein with respect to FIGS. 1-6. In accordance with theprinciples of the present invention, methods of manufacturing a hybridcontact lens by chemical bonding will now be described with respect toFIGS. 12-29. More particularly, the methods pertain to chemicallybonding a substantially flexible hydro-gel soft skirt portion to asubstantially rigid high or hyper DK gas permeable core center portion.

Suitable materials for the substantially flexible portion include, butare not limited to: hydroxyethylmethacrylate (HEMA); methyl methacrylate(MMA); Ethyl methacrylate (EMA); butylmethacrylate (BMA),Hexylmethacrylate (HMA), ehtylacrylate (EA), butylacrylate (BA),aminoaklyl containing acrylate or methacrylate; N-vinyl pyrrolidone(NVP); 2-methoxyethyl methacrylate (MEMA); ethylene glycol methacrylate(EGMA); trifluoropropyl methacrylate; pentafluoropentyl methacrylate;N,N-dimethylacrylamide (DMA); acrylamide; methacylamide;tetramethyldisiloxane ethylene glycol dimethacrylate; perfluorophenylmethacrylate; 2-(trimethylsiloxyl)ethyl methacrylate; N-fluoroalkylmethacylamide; bis(2-methacryloxyphenyl)propane;(N,N-dimethylamino-ethyl)methacrylate; silicon hydrogels such asCibavision lotrafilcon; and any combination of these materials. As wouldbe understood to those of ordinary skill in the art, the above list isby no means exhaustive as other soft skirt materials may be employed asthe substantially flexible portion without departing from the scope ofthe present invention.

Suitable materials for the substantially rigid portion include, but arenot limited to: fluorosilicone acrylate; siliconated, styrene;fluoroacrylate; fluorometharylate, perfluorianted acrylate andmethacrylate; any high DK or hyper DK gas permeable rigid contact lensbottoms with DK of 70 (ISO), such as Boston 7 Envision, Boston EO,Boston Equales, Boston Equalens 2, Boston XO, HDS 60, HDS 100,Fluoroperm 151, Fluoroperm 92, Fluoroperm 92, Fluoro 700, Menicon SE-P,Menicon Z; any other high DK materials; and any combination of thesematerials. Of course, as would be understood to those of ordinary skillin the art, this list is by no means exhaustive as other materials maybe employed as the substantially rigid portion without departing fromthe scope of the present invention.

A method of manufacturing a hybrid contact lens using a molded cup willnow be described with respect to FIGS. 12-15. Referring to FIG. 12,molded cup 100 comprises horizontal surface 102, a cylindrical outerwall 104 disposed substantially normal to horizontal surface 102 and acylindrical inner wall 106. The area within inner wall 106 comprises acylindrical inner section 109 for receiving substantially rigidmaterial, and the area between the inner and outer walls comprises acylindrical outer section 111 for receiving substantially flexiblematerial.

Inner wall 106 preferably comprises a pre-form optical grade dividerthat divides the substantially rigid inner portion and the substantiallyflexible outer portion. In addition, inner wall 106 preferably isbondable with both rigid and flexible materials used to form the contactlens. Suitable materials for the molded cup include, but are not limitedto, polypropylene, polyethylene, polyethylene terephthalate (PET),polycarbonate and optical grade plastics. The inner and outer wallsoptionally are coated with an adhesive to promote bonding with theflexible and rigid portions.

Preferably, a thin portion of the molded cup remains part of thefinished contact lens. Alternatively, portions of the molded cup may beremoved during the casting process. For example, inner wall 106 may beremoved after pouring and curing the substantially rigid portion, andouter wall 104 may be removed after pouring and curing the substantiallyflexible portion. According to some embodiments, molded cup 100 furthercomprises a lower cylinder 108 that forms lower section 113, which isdimensioned to produce a gripping area that conforms to the collet of acomputer numerically controlled lathe or other machining apparatus. Inthese embodiments, horizontal surface 102 preferably includes a centralopening 110 such that lower section 113 may be filled duringmanufacturing. Alternatively, lower section 113 may be pre-filled beforemanufacturing. According to other embodiments, lower cylinder 108 is notprovided.

In the illustrated embodiment, inner wall 106 or divider 106 is disposedat an angle A with respect to horizontal surface 102. Angle A may be anyangle from about 5 degrees to about 175 degrees, but preferably isselected to maximize the bonding strength between the rigid and flexibleportions of the contact lens. Inner wall 106 optionally includes a bendB adapted to further increase the bonding strength between the rigid andflexible portions. As would be understood to those of ordinary skill inthe art, many alternative inner wall configurations may be employedwithout departing from the scope of the present invention. For example,examples of alternative bonding angles between the flexible and rigidportions are described above with respect to FIGS. 6 and 6A.Additionally, examples of alternative inner wall configurations will nowbe described.

Referring to FIG. 13A, molded cup 100 includes an alternative inner wall114 that is disposed substantially normal to horizontal surface 102(i.e., angle A is about 90 degrees). In addition, inner wall 114 doesnot include a bend. Referring to FIG. 13B, molded cup 100 includes analternative inner wall 116 that is disposed at an acute angle withrespect to horizontal surface 102. Referring to FIG. 13C, molded cup 100includes an alternative inner wall 118 that is disposed at an obtuseangle with respect to horizontal surface 102. Referring to FIG. 13D,molded cup 100 includes an alternative inner wall 120 including aplurality of bends B. Bends B preferably increase the bonding strengthbetween the rigid and flexible portions. Additionally, inner wall 120 isdisposed at an angle A with respect to horizontal surface 102. Similarto the embodiment disclosed above with respect to FIG. 12, angle A maybe any angle from about 5 degrees to about 175 degrees, but preferablyis selected to maximize the bonding strength between the rigid andflexible portions of the contact lens.

Referring to FIG. 14, a predetermined amount of liquefied resin ofsubstantially rigid material is poured within inner section 109 suchthat the material: (1) fills lower section 113 via opening 110, therebyforming gripping area 128; and (2) substantially fills inner section109, thereby forming substantially rigid portion 126. Then, the moldedcup is placed into a programmed curing environment and the rigidmaterial is cured with heat, UV light, or a combination of both.

Alternatively, a predetermined amount of liquefied resin ofsubstantially rigid material is poured within inner section 109 suchthat the material only fills lower section 113, thereby forming grippingarea 128. Then, the molded cup is placed into a programmed curingenvironment and the rigid material is cured with heat, UV light, or acombination of both. After curing, an additional predetermined amount ofliquefied resin of rigid material is poured within inner section 109such that the additional material substantially fills inner section 109,thereby forming substantially rigid portion 126. Then, the molded cup isagain placed into the programmed curing environment and the rigidmaterial is cured with heat, UV light, or a combination of both.

Referring to FIG. 15, after curing the substantially rigid material, apredetermined amount of liquefied resin of substantially flexiblematerial is poured into outer section 111, thereby forming substantiallyflexible portion 130. Then, the molded cup is again placed into theprogrammed curing environment and the flexible material is cured withheat, UV light, or a combination of both. After curing the flexiblematerial, the lens is ready to be lathed, or otherwise machined, into afinished, fracture-resistant hybrid contact lens.

A method of manufacturing a hybrid contact lens using a block mold willnow be described with respect to FIGS. 16-21. Referring to FIG. 16,block mold 134 comprises a pair of halves 136, 138 that are attachedalong a breaking plane 140. Block mold halves 136, 138 preferably aresymmetric about breaking plane 140. Block mold 134 further comprises acentral void 144, 146 that defines an upper section 144 and a lowersection 146. Central void 144, 146 forms an opening 150 in asubstantially horizontal top surface 152 of block mold 134 such that theupper and lower sections may be filled with liquefied resin of the rigidmaterial to form the hard portion of the contact lens.

According to some embodiments, lower section 146 preferably isdimensioned to produce a gripping area that conforms to the collet of acomputer numerically controlled lathe or other machining apparatus. Inthese embodiments, an opening 148 exists between the upper and lowersections such that lower section 146 may be filled with liquefied resinduring manufacturing. According to other embodiments, lower section 146is not provided.

Upper section 144 includes an outer wall 156 formed by an inside surfaceof the block mold halves. Outer wall 156 forms the shape of the junctionbetween the rigid and flexible portions of the contact lens. In theillustrated embodiment, outer wall 156 is disposed at an angle A withrespect to top surface 152. Angle A may be any angle from about 5degrees to about 175 degrees, but preferably is selected to maximize thebonding strength between the rigid and flexible portions of the contactlens. Outer wall 156 optionally includes a bend B adapted to furtherincrease the bonding strength between the rigid and flexible portions.As would be understood to those of ordinary skill in the art, manyalternative outer wall configurations may be employed without departingfrom the scope of the present invention. Some of these alternative outerwall configurations will now be described.

Referring to FIG. 17A, upper section 144 of the central void includes analternative outer wall 158 that is disposed substantially normal tohorizontal surface 152 (i.e., angle A is about 90 degrees). In addition,outer wall 158 does not include a bend. Referring to FIG. 17B, uppersection 144 includes an alternative outer wall 160 that is disposed atan acute angle with respect to horizontal surface 152. Referring to FIG.17C, upper section 144 includes an alternative outer wall 162 that isdisposed at an obtuse angle with respect to horizontal surface 152.Referring to FIG. 17D, upper section 144 includes an alternative innerwall 164 including a plurality of bends B. Bends B preferably increasethe bonding strength between the rigid and flexible portions of thecontact lens.

Referring to FIG. 18, a predetermined amount of liquefied resin ofsubstantially rigid material is poured into opening 150 such that thematerial: (1) fills the area within lower section 146, thereby forminggripping area 172; and (2) substantially fills upper section 144,thereby forming substantially rigid section 170. Then, the block mold isplaced into a programmed curing environment and the rigid material iscured with heat, UV light, or a combination of both. Alternatively, apredetermined amount of liquefied resin of substantially rigid materialis poured into opening 150 such that the material only fills the areawithin lower section 146, thereby forming gripping area 172. Then, theblock mold is placed into a programmed curing environment and thesubstantially rigid material is cured with heat, UV light, or acombination of both. After curing, an additional predetermined amount ofliquefied resin of rigid material is poured into opening 150 tosubstantially fill upper section 144, thereby forming substantiallyrigid section 170. Then, the block mold is again placed into theprogrammed curing environment and the rigid material is cured with heat,UV light, or a combination of both.

Referring to FIG. 19, after curing the substantially rigid material,block mold 134 is broken along breaking plane 140 and the cured sectionof rigid material (comprising rigid section 170 and gripping area 172)is removed from the block mold halves. At this point, the surface of thecured section of rigid material optionally is primed or coated forbetter bonding. Referring to FIG. 20, a guard 178, 180 comprising asubstantially horizontal section 178 and a cylindrical sidewall 180 isattached on top of gripping area 172 using a suitable adhesive.Referring to FIG. 21, a predetermined amount of liquefied resin offlexible material is then poured into the area between rigid section 170and sidewall 180, thereby forming substantially flexible portion 182.

With further reference to FIG. 21, the materials are then placed intothe programmed curing environment and the substantially flexiblematerial is cured with heat, UV light, or a combination of both. Thehybrid materials (i.e., rigid section 170 and flexible section 182) arenow primed to be lathed, or otherwise machined, into a finished,fracture-resistant hybrid contact lens. Unlike the embodiment disclosedwith respect to FIGS. 12-15, there is no wall or divider disposedbetween the rigid and flexible portions.

A method of manufacturing a hybrid contact lens using a base curve moldwill now be described with respect to FIGS. 22-24. Referring to FIG. 22,base curve mold assembly 190 comprises base curve mold 192, inner wall194 or divider 194, outer wall 196 disposed around the outercircumference of base curve mold 192. Optionally, one or more centeringwebs 198 are provided between the inner and outer walls to ensure properpositioning of inner wall 194 with respect to a vertically disposed baseplane 200 that passes through the center of base curve mold 192. Innerwall 194 acts as a separator and junction surface between the rigid andflexible materials. Inner wall 194 preferably is a pre-form opticalgrade divider that is bondable with both rigid and flexible materialsused to form the contact lens. According to some embodiments, inner wall194 is coated with an adhesive to promote bonding with the rigid andflexible portions.

In the illustrated embodiment, inner wall 194 is substantiallyvertically disposed (i.e., parallel to plane 200). However, similar tothe embodiments described above with respect to FIGS. 12-21, inner wall194 may be disposed at any angle from about 5 degrees to about 175degrees with respect to a horizontal plane. Through the process of trialand error an angle may be chosen that maximizes bonding strength betweenthe rigid and flexible portions of the contact lens. Inner wall 194optionally includes one or more bends B adapted to further increase thebonding strength. Of course, as would be understood to those of ordinaryskill in the art, many alternative inner wall configurations may beemployed without departing from the scope of the present invention.

Referring to FIG. 23, a predetermined amount of liquefied resin ofsubstantially rigid material is poured within inner wall 194 to fill thearea therebetween, thereby forming substantially rigid portion 202.Then, the base curve mold assembly is placed into a programmed curingenvironment and the rigid material is cured with heat, UV light, or acombination of both. Referring to FIG. 24, after curing the rigidmaterial, a predetermined amount of liquefied resin of substantiallyflexible material is poured into the area between inner wall 194 andouter wall 196, thereby forming substantially flexible portion 204.Then, the base curve mold assembly 190 is again placed into theprogrammed curing environment and the flexible material is cured withheat, UV light, or a combination of both. After curing the flexiblematerial, the outer wall and centering webs are removed and the anteriorsurface of the lens is ready to be lathed, or otherwise finished.

A method of manufacturing a hybrid contact lens using a base curve blockmold assembly will now be described with respect to FIGS. 25-29.Referring to FIG. 25, base curve block mold assembly 210 comprises basecurve mold 212 and a pair of block mold halves 214, 216 that aresymmetrically disposed about a vertical plane 218 passing through thecenter of base curve mold 212. Base curve block mold assembly 210further comprises a central void 222 disposed in the area above basecurve mold 212 between block mold halves 214, 216. Central void 222 isadapted to be filled with liquefied resin of the rigid material to formthe hard portion of the contact lens.

Central void 222 includes an outer wall 226 formed by an inside surfaceof the block mold halves. Outer wall 226 forms the shape of the junctionbetween the rigid and flexible portions of the contact lens. In theillustrated embodiment, outer wall 226 is disposed substantiallyparallel to vertical plane 218. However, similar to the embodimentsdescribed above with respect to FIGS. 12-24, outer wall 226 may bedisposed at any angle from about 5 degrees to about 175 degrees withrespect to a horizontal plane. Through the process of trial and error anangle may be chosen that maximizes bonding strength between the rigidand flexible portions of the contact lens. Additionally, outer wall 226optionally includes one or more bends B adapted to further increase thebonding strength. Of course, as would be understood to those of ordinaryskill in the art, many alternative outer wall configurations may beemployed without departing from the scope of the present invention.

Referring to FIG. 26, a predetermined amount of liquefied resin ofsubstantially rigid material is poured into central void 222 such thatthe material fills the area within central void 222, thereby formingsubstantially rigid section 230. Then, the block mold is placed into aprogrammed curing environment and the rigid material is cured with heat,UV light, or a combination of both. Referring to FIG. 27, after curingthe rigid material, block mold halves 214, 216 are separated and removedfrom base curve mold 212. Referring to FIG. 28, a curvilinear sidewall234 is attached around the perimeter of base curve mold 212 using asuitable adhesive.

Referring to FIG. 29, a predetermined amount of liquefied resin ofsubstantially flexible material is then poured into the area betweenrigid section 230 and sidewall 234, thereby forming substantiallyflexible portion 236. The materials are then placed into the programmedcuring environment and the flexible material is cured with heat, UVlight, or a combination of both. After curing the flexible material, thesidewall is removed and the anterior surface is lathed, or otherwisefinished.

A method of manufacturing a hybrid contact lens using a using apre-shape mold assembly including a pre-machined substantially rigidcenter portion as a molded insert of a soft-skirt mold will now bedescribed with respect to FIGS. 30-33. Referring to FIG. 30,substantially rigid center portion 250 is formed and cured before beingplaced in the mold assembly. According to some embodiments, the rigidcenter portion is pre-coated or pre-treated with an adhesive to promotebonding with the flexible outer portion. Referring to FIG. 31, pre-shapemold assembly 252 comprises a base curve mold 254 and a pair of blockmold halves 256, 258 that are symmetrically disposed about a verticalplane 260 passing through the center of base curve mold 254.

Pre-shape mold assembly 252 further comprises a substantiallybowl-shaped void 264 disposed between the base curve mold and the blockmold halves. Bowl-shaped void 270, 272 comprises an inner portion 270for receiving substantially rigid center portion 250 and an outerportion 272 that is filled with a substantially flexible material. Inaddition, pre-shape mold assembly 252 preferably includes a central void266 disposed in the area above base curve mold 254 between block moldhalves 256, 258. Central void 266 is dimensioned to permit thesubstantially rigid center portion to be inserted into inner portion 270after it is formed and cured. One or more injection apertures 274preferably are provided in the pre-shape mold assembly for filling theouter portion of bowl-shaped void 270, 272.

Referring to FIG. 32, a predetermined amount of liquefied resin ofsubstantially rigid material is injection into outer portion 270,thereby forming substantially flexible outer portion 276. Then,pre-shape mold assembly 252 is placed into a programmed curingenvironment and the flexible material is cured with heat, UV light, or acombination of both. Referring to FIG. 33, after curing the flexiblematerial, the mold is separated and the finished contact lens is removedfrom the mold. According to some embodiments, the contact lens mayrequire machining of the anterior or posterior surfaces before it isready for use.

As disclosed above with respect to FIG. 6, the bonding angle between theflexible and rigid portions of the contact lens may vary from almost 0degrees to almost 90 degrees. In addition, the interface between theflexible and rigid portions may include a variety of surfaceconfigurations, including, but not limited to, ledges, protuberances,substantially V- or W-shaped projections, serrations, gradations, andany other shape that is not substantially straight, or planar.Alternatively, as disclosed above with respect to FIG. 6A, a junctionmay be provided between flexible and rigid portions.

With further reference to FIGS. 30-33, the substantially rigid portionmay comprise one or more of the following monomers, monomer mixtures,and their derivatives: trimeththylsiloxyl; methyl-methacrylate;ethyl-methacrylate; ethylene glycol di-methacrylate; octafluoropentyl-methacrylate; tetra-methyldisiloxane; ethylene glycoldi-methacrylate; pentafluoro phenylacrylate; 2-(trimethylsiloxyl)methacrylate; bis(2-metharyloxyphenyl) propane;N-[2-(N,N-dimethylamino)ethyl]; onethacrylate;N-[2-(n,n-dimethylamino)ethy]; methacryalte; vinylpyrolidone;N,N-dimathacrylamide; acrylamine; hydroxyethyl methacrylate; siloxaneethylene glycol di-methacrylate; trifluoroethyl methacrylate;pentafluorostyrene; pentafluoropropyl methacrylate; unsaturatedpolyester; p-vinyl benzyl hexafluoroisopropyl ether;siloxanylalkylamide; and combinations thereof. As would be understood tothose of ordinary skill in the art, many other materials may be used toform the substantially rigid portion without departing from the scope ofthe present invention.

For the embodiment disclosed with respect to FIGS. 30-33, thesubstantially flexible portion may comprise one or more of the followingmonomer mixtures and their derivatives: poly HEMA; hydroxyethylacrylate; dihydroxypropyl methacrylate; polyethylaneglycol;methylmethacrylate, ethyl methacrylate, butylmethacrylate (BMA),Hexylmethacrylate (HMA), ehtylacrylate (EA), butylacrylate (BA),acetoxysilane; trimethylesiloxy; ethyleneglycol-dimethacrylate;phenylethyl acrylate; zero-gel; Silicon-Hydrogel; polyethylene oxide;and combinations thereof. As would be understood to those of ordinaryskill in the art, many other materials may be used to form thesubstantially flexible portion without departing from the scope of thepresent invention.

For the embodiment disclosed with respect to FIGS. 30-33, the pre-treator pre-coat between flexible and rigid portions of the contact lens maycomprise an adhesive or resin on or more of the following monomermixtures and their derivatives: vinylacetate; trifluoroethanol;methacrylates (C1 to C6); acrylates (C1 to C6); ethanediamine;2-hydroxyethylmethacrylate (HEMA) and other esters of methacrylic acidformulated from acrylic bases; fluorine; silicone; fluorine/silicone;styrene and resultant polymers such as polystyrene; fluorine/styrene;silicone/styrene; and combinations thereof. As would be understood tothose of ordinary skill in the art, many other materials may be used toform pre-treat or pre-coat without departing from the scope of thepresent invention.

Further methods of manufacturing a hybrid contact lens according to thepresent invention involve pouring the rigid and flexible materials inthe reverse order such that the flexible material is poured and curedbefore the rigid material. For the block mold embodiments, this willrequire the creation of blocks that fill the central void such that theouter, flexible portion may be poured and cured first. Additionalmethods involve pouring both rigid and flexible materials atsubstantially the same time, then curing the materials simultaneously.

Additional methods of manufacturing a hybrid contact lens according tothe present invention involve molding or lathing a standard base curvemold with a standard or semi-customized front surface, then using athermal or laser energy to modify the refractive index of the centermaterial to a desired optical requirement. Advantageously, these methodsreplace expensive custom lathing and molding operations. Further methodsinvolve molding both the posterior and anterior surfaces of the contactlens. Other methods involve the application of a mechanical force orthermal molding.

Alternative manufacturing methods of the present invention may include:molding of the posterior surface and diamond turning of the moldedblank; contour cutting of the anterior surface of a posterior curvefinished blank; etching the anterior or posterior surface of a posteriorcurve finished blank or predicate lens anterior or posterior surface;thin film deposition of a predicate lens anterior or posterior surface;and laser ablation of a predicate lens anterior or posterior surface.

A preferred method of manufacturing a hybrid contact lens by chemicallybonding the substantially flexible portion to the substantially rigidportion will now be described with respect to FIGS. 34-40. It is herebynoted that any of the above-described molding methods and technologiesmay be employed in conjunction with the below-described method.Initially, the substantially rigid portion is formed by casting a rod ofsubstantially rigid, gas permeable, high (or hyper) DK material havingthe desired characteristics. After curing, the rod is precision groundto produce a substantially uniform diameter. Referring to FIG. 34, therod is then machined into a primary blank that forms the substantiallyrigid portion 300 of the contact lens. A middle section 302 ofsubstantially rigid portion 300 is simultaneously machined to have apredetermined configuration forming the interface of the rigid andhydrophilic material in the finished lens.

Referring to FIG. 35, after the substantially rigid portion 300 has beenmachined, the resulting blank is placed within a cup 308. Cup 308comprises a bottom surface 310 and an outer wall 312, and optionally mayinclude a lathe gripping area. The substantially rigid portion 300preferably is attached to bottom surface 310 using an adhesive such asepoxy resin or other adhesive. Referring to FIG. 36, the next stepinvolves treating the substantially rigid portion to promote adhesion tothe soft skirt portion. This step entails the steps of pouring achemical solution 316 into the cup 308, soaking the rigid portion for apredetermined amount of time and applying a catalyst to the rigidportion. According to some embodiments, the chemical solution 316contains a hompolymer such as methyl methacrylate (MMA) and thepredetermined soaking time is from about 1 second to about 20 minutes,most preferably about 30 seconds.

After soaking is completed, the chemical solution 316 is removed fromthe cup 308 by way of a suction pump or other drainage device. Referringto FIG. 37, a coating 318 is formed on the perimeter of thesubstantially rigid portion 300 by applying a catalyst thereto. Thecatalyst preferably is a UV activator (e.g., UV light) applied to therod for a predetermined curing time of about 1 minute to about 60minutes, most preferably about 30 minutes. Advantageously, coating 318facilitates subsequent bonding between the soft and hard portions of thecontact lens. Moreover, coating 318 slows the penetration of thechemical solution into substantially rigid portion 300. Excessivepenetration of the chemical solution into the rod alters the physicalcharacteristics of the sensitive high DK center portion. Specificphysical characteristics of the high DK center portion that may beaffected include oxygen permeability, index of refraction, modulus andother physical characteristics. As an alternative to forming the coatingto protect the rod, an intermediate material may be employed to protectthe hard center from excessive chemical penetration.

Referring to FIG. 38, the next step involves treating the coating tofurther promote adhesion to the substantially flexible material. Thisstep entails softening the coating by pouring a chemical solution 320into the cup 308 and soaking the substantially rigid portion 300 for apredetermined amount of time. Chemical solution 320 preferably containsMMA. In addition, the predetermined soaking time preferably is fromabout 5 seconds to about 20 minutes, most preferably for about 15seconds. Softening the coating further facilitates subsequent bondingbetween the soft and hard materials that form the hybrid contact lens.After soaking is completed, the chemical solution 320 is removed fromthe cup 308 by way of a suction pump or other drainage device.

Referring to FIG. 39, the next step involves further treating thecoating to promote adhesion to the substantially flexible material. Thisstep entails pouring another chemical solution 324 into cup 308 andsoaking the substantially rigid portion 300 for a predetermined amountof time. Chemical solution 324 preferably contains MMA, as well as anadhesion promoter and a UV activator. The predetermined amount of timefor soaking is from about 5 second to about 20 minutes, most preferablyfor about 15 seconds. Depending upon the type of material used for thesubstantially rigid portion 300, the above-disclosed soaking steps maybe performed in a different order. Alternatively, one or more of thesoaking steps may be eliminated depending upon the substantially rigidmaterial employed.

After the soaking steps are completed, the chemical solution 324 isremoved from the cup 308 by way of a suction pump or other drainagedevice. Then, excess chemical solution on the substantially rigidportion 300 is removed by spinning. According to some embodiments,spinning is carried out for approximately 6 seconds at a speed of 1350rpm or greater. Referring to FIG. 40, the next steps involve pouringliquefied substantially flexible material 330 into the cup 308 aroundthe substantially rigid center portion and curing the substantiallyflexible material 330. Preferably, the time between pouring and curingis kept to a minimum, for example less than 1 minute.

The step of curing the substantially flexible material 330 is achievedby applying a UV activator to the mold for a predetermined curing time.Preferably, a slow cure is performed under a low dose of visible UVlight for approximately 45 minutes. In the next step, UV curing andthermal annealing are performed simultaneously for about 2 to 3 hours.After this time period, UV curing is discontinued and thermal annealingis sustained for an additional period of time, preferably about 10 to 20hours, most preferably about 15 hours. This slow cure annealing stepadvantageously creates improved bonding strength and more uniform lenssurfaces while reducing undesirable stresses within the lens. Accordingto some embodiments, the thermal annealing step is performed over adefined heating/cooling profile wherein the mold is slowly heated fromroom temperature until reaching a peak temperature, and then slowlycooled back to room temperature.

Referring to FIGS. 41 and 42, after curing the flexible material, thelens is lathed or otherwise machined into a finished fracture-resistanthybrid contact lens 332 comprising substantially rigid center portion300 and substantially flexible outer skirt portion 330. In theillustrated embodiment, center portion 300 and outer skirt portion 330are joined at junction 334 that is substantially V-shaped in crosssection. As depicted in FIG. 42, junction 334 is defined by a firstsegment 338 and a second segment 340, which are disposed at an angle Awith respect to one another. Moreover, segment 338 is disposed at anangle B with respect to an anterior surface 342 of the lens and segment340 is disposed at an angle C with respect to a posterior surface 344 ofthe lens.

According to some embodiments, the dimensions defining the V-shapedinterface are selected to reduce the variance in expansion of the softskirt near the junction, thereby improving the comfortability of thelens. Generally, less expansion of the soft skirt material results in asmoother transition between the soft and hard portions. Since theexpansion of the soft skirt material is a percentage of the materialthickness, angles A, B and C are chosen to limit the amount of softskirt material in a transition area 348 encompassing junction 334. AngleA may be any angle between about 5 degrees and about 175 degrees,preferably between about 15 degrees and about 90 degrees, mostpreferably about 80 degrees. Angle B may be any angle between about 5degrees and about 175 degrees, preferably between about 100 degrees andabout 165 degrees, most preferably about 140 degrees. Angle C may be anyangle between about 5 degrees and about 175 degrees, preferably betweenabout 100 degrees and about 165 degrees, most preferably about 140degrees.

An additional advantage of providing a V-shaped junction is theresultant increase in surface area between the rigid and soft skirtcomponents improves bonding strength between the two materials andminimizes lens breakage, or failure. A further advantage is that theanterior and posterior surfaces of the transition area 348 consistprimarily of the substantially flexible material 330, which providesincreased comfort for the user. According to alternative embodiments,junction 334 may comprise a single segment disposed at an angle withrespect to the contact lens, as disclosed with respect to FIG. 6. Inaddition, junction 334 may include a variety of surface configurations,or geometries, such as including ledges, protuberances, or projections,serrations, gradations, or any other shape that is not substantiallystraight, or planar.

Suitable materials for the substantially flexible portion 330 include,but are not limited to: hydroxyethylmethacrylate (HEMA); methylmethacrylate (MMA); Ethyl methacrylate (EMA); aminoaklyl containingacrylate or methacrylate; N-vinyl pyrrolidone (NVP); 2-methoxyethylmethacrylate (MEMA); ethylene glycol methacrylate (EGMA);trifluoropropyl methacrylate; pentafluoropentyl methacrylate; N,N-dimethylacrylamide (DMA); acrylamide; methacylamide;tetramethyldisiloxane ethylene glycol dimethacrylate; perfluorophenylmethacrylate; 2-(trimethylsiloxyl)ethyl methacrylate; N-fluoroalkylmethacylamide; bis(2-methacryloxyphenyl)propane;(N,N-dimethylamino-ethyl)methacrylate; silicon hydrogels such asCibavision lotrafilcon; and any combination of these materials. As wouldbe understood to those of ordinary skill in the art, the above list isby no means exhaustive as other soft skirt materials may be employed asthe substantially flexible portion without departing from the scope ofthe present invention.

Suitable materials for the substantially rigid portion 300 include, butare not limited to: fluorosilicone acrylate; siliconated, styrene;fluoroacrylate; fluorometharylate, perfluorianted acrylate andmethacrylate; any high DK or hyper DK gas permeable rigid contact lensbottoms with DK of 70 (ISO), such as Boston 7 Envision, Boston EO,Boston Equales, Boston Equalens 2, Boston XO, Fluoroperm 151, Fluoroperm92, Fluoroperm 92, Fluoro 700, Menicon SE-P, Menicon Z; any other highDK materials; and any combination of these materials. Of course, aswould be understood to those of ordinary skill in the art, this list isby no means exhaustive as other materials may be employed as thesubstantially rigid portion without departing from the scope of thepresent invention.

Referring to FIGS. 43-48 a hybrid contact lens manufactured using themethods of the present invention comprises three or more zones havingdifferent properties and compositions. Referring to FIGS. 43 and 44,hybrid contact lens 360 comprises central zone 362, peripheral zone 364and intermediate zone 366. Similar to previous embodiments, central zone362 preferably comprises a substantially rigid, gas permeable, high orhyper DK material such as fluoro-siloxane acrylate, siloxane acrylate,or poly-stryene siloxane acrylate. Additionally, any of the previouslydisclosed high DK and hyper DK materials may be used to form centralzone 362. Likewise, peripheral zone 364 preferably comprises asubstantially flexible hydro-gel material such as HEMA, MMA, or EMA. Ofcourse, peripheral zone 364 may also comprise any of the previouslydisclosed substantially flexible hydro-gel materials.

Intermediate zone 366 is a thin film or coating formed on the perimeterof central zone 362 during lens manufacture. Advantageously, the film orcoating defined by intermediate zone 366 facilitates subsequent chemicalbonding between the central and peripheral zones. Further, intermediatezone 366 provides a protective barrier from the soft peripheral zonematerials, thereby preventing potentially deleterious modification ofthe physical characteristics of the sensitive high DK central zone, suchas including oxygen permeability, index of refraction, modulus and otherphysical characteristics. Intermediate zone 366 is formed by soaking thecentral zone in a chemical solution containing oligomer acrylatemonomers for a predetermined amount of time. In a preferred embodiment,the central zone is a first material (e.g., a high or hyper DK, gaspermeable material such as fluoro-siloxane acrylate), the peripheralzone is a second material (i.e., a substantially flexible hydro-gelmaterial such as HEMA), whereas the intermediate zone formed by the fileis a third material (e.g., MMA).

A method of forming a hybrid contact lens according to the principles ofthe present invention comprising the steps of forming a central zone,forming a protective barrier around the central zone and chemicallybonding a peripheral zone to the central zone. The protective barrierfacilitates subsequent chemical bonding between the central andperipheral zones, and also prevents modification of the physicalcharacteristics of the central zone. The central zone preferablycomprises a substantially rigid, gas permeable material that is a highDK material having a DK value between about 30 and about 250. Accordingto some embodiments, the substantially rigid, gas permeable material isa hyper DK material having a DK value of at least 250.

The depth of penetration of the chemical solution into the central zonepreferably is controlled as a function of soaking time. A catalyst suchas a UV activator may also be employed to promote the creation ofintermediate zone 366. The acrylate solution preferably contains one ormore of the following monomers: methyl methacrylate; ethyl methacrylate;butyl methacrylate; hexylmethacrylate; T-butylaminoethylmethacrylate;T-Butylaminoethylacrylate; dimethylaminoethyl acrylate; methacrylate, d;fluorinated acrylate; methacrylates including hexafluoro methacryalte,2,2,2-trifluoroethylmethacrylate, 1,1-dihydropropyloctylmethacryalte,hexafluoroisopropyl acryalte and methacrylate, acrylate and methacrylate(mono and di) of perfluorinated ether; silicone containing methacylateincluding 3-methacryloxypentamethyldisiloxane,3-methylacryloxypropyltris (trimethylsiloxy)silane,3-methacryloxypropyltrimethoxysilane, 5-N,N-dimehylacrylamide,N-vinylprolidone, vinyl acetatem 2-ethylhexyl methacrylate, methyl andbutylacrylate and methacrylate; epoxy acrylates; urethane acrylates;carboxylic acid half esters; polyester acrylates; acrylated acrylics;low viscosity oligomers poly(ethylene glycol) acrylate and methacrylate(mono and di); poly(propylene glycol) acrylate and methacrylate (monoand di); diacrylate and dimethyacrylate of polydimethylsiloxanr (M.Wt2000-4000); and combinations thereof.

According to some embodiments of the present invention, intermediatezone 366 is softened by being soaked in a chemical solution containingacrylate monomers and an adhesion promoter for a predetermined amount oftime. Suitable adhesions promoters include, but are not limited to,epoxy acrylates, urethane acrylates, carboxylic acid half esters,polyester acrylates, acrylated acrylics and low viscosity monomers.After the intermediate zone has been formed, a spinning process may beused to remove excess chemical solution. As described above with respectto FIGS. 34-42, one or more curing steps may be employed to cure theintermediate zone prior to forming the peripheral zone.

With further reference to FIGS. 43 and 44, intermediate zone 366 isdisposed at an angle that is substantially normal to anterior surface372 and posterior surface 374 of hybrid contact lens 360. According toother embodiments, intermediate zone 366 is disposed at an angle otherthan 90 degrees with respect to the lens such that a transition isthereby provided. For most lenses, the thickness of intermediate zone366 preferably is between about 200 nm to about 500 nm. However,according to some embodiments, the thickness may be increased to 2 mm ormore. As would be understood to those of skill in the art, many otherintermediate zone thicknesses are possible without departing from thescope of the present invention. According to other embodiments,intermediate zone 366 may be disposed at an angle (other than normal)with respect to the contact lens, as disclosed with respect to FIG. 6.Additionally, intermediate zone 366 may include a variety of surfaceconfigurations, or geometries, such as including ledges, protuberances,or projections, serrations, gradations, or any other shape that is notsubstantially straight, or planar.

Referring to FIGS. 45 and 46, hybrid contact lens 380 comprises centralzone 382, peripheral zone 384 and intermediate zone 386, whereinintermediate zone 386 is a thin curvilinear film or coating disposedbetween the central and peripheral zones. Intermediate zone 386 is athin film or coating formed on the perimeter of the central zone duringlens manufacture. Similar to previous embodiments, central zone 382preferably comprises a substantially rigid, gas permeable, high (orhyper) DK material and peripheral zone 384 preferably comprises asubstantially flexible hydro-gel material. Curvilinear intermediate zone386 comprises a convex surface 390 that faces peripheral zone 384 and aconcave surface 392 that faces central zone 382.

As depicted in FIG. 46, hybrid contact lens 380 includes a transitionarea 396 that comprises intermediate zone 386 and a portion of thecentral and peripheral zones. Similar to the above-described V-shapedjunction, curvilinear intermediate 386 zone preferably is dimensioned toreduce the variance in expansion of the peripheral zone within thetransition area. Generally, less expansion of the peripheral zonematerial results in a smoother transition between the soft and hardportions. Since the expansion of the peripheral zone material is apercentage of the material thickness, the radius of curvature ofintermediate zone 386 chosen to limit the amount of peripheral zonematerial within transition area 386. According to some embodiments, theradius of curvature is chosen such that the percentage of peripheralzone material within the transition area preferably is less than about30 percent, most preferably less than about 20 percent. In theillustrated embodiment, convex surface 390 abuts against peripheral zone384 (conversely, concave surface 392 abuts against central zone 382)such that only a small amount of soft peripheral zone material isdisposed within transition area 396.

An additional advantage of providing a curvilinear intermediate zone isthe resultant increase in surface area between the central andperipheral zones improves bonding strength between the respectivematerials and minimizes lens breakage, or failure. A further advantageis that the anterior and posterior surfaces of transition area 386consist primarily of the more comfortable substantially flexiblematerial. According to other embodiments, transition area 386 mayinclude a variety of surface configurations, or geometries, such asincluding ledges, protuberances, or projections, serrations, gradations,or any other shape that is not substantially straight, or planar.

Referring to FIGS. 47 and 48, hybrid contact lens 400 comprises centralzone 402, peripheral zone 404, first intermediate zone 406 and secondintermediate zone 408. Intermediate zones 406, 408 are thin films orcoatings disposed between the central and peripheral zones. Similar toprevious embodiments, central zone 402 preferably comprises asubstantially rigid, gas permeable, high (or hyper) DK material andperipheral zone 404 preferably comprises a substantially flexiblehydro-gel material. First intermediate zone 406 is a thin film orcoating formed on the perimeter of central zone 402 during lensmanufacture. Likewise, second intermediate zone 408 is a thin film orcoating formed on the perimeter of first intermediate zone 406. Theintermediate zones advantageously facilitate chemical bonding betweenthe central and peripheral zones and also provide a barrier to protectthe central zone from the soft peripheral zone materials during lensmanufacture. It is well known that high DK materials are generallysensitive to temperature

As depicted in FIG. 48, hybrid contact lens 400 includes a transitionarea 412 that comprises first and second intermediate zones 406, 408.Intermediate zone 406 is formed by soaking the central zone in a firstchemical solution containing oligomer acrylate monomers for apredetermined amount of time, thereby forming first intermediate zone406. The central zone is then soaked in a second chemical solutioncontaining oligomer acrylate monomers for a predetermined amount oftime, thereby forming second intermediate zone 408. The acrylatesolutions preferably contain one or more of the following monomers:methyl methacrylate; ethyl methacrylate; butyl methacrylate; andhexylmethacrylate. According to some embodiments, the first and secondchemical solutions contain substantially the same chemicals. Accordingto other embodiments, the first and second chemical solutions containdifferent chemicals. A catalyst such as a UV activator may be employedto promote the creation of intermediate zones 406, 408.

According to some embodiments of the present invention, the intermediatezones are softened by being soaked in a chemical solution containingacrylate monomers and/or an adhesion promoter for a predetermined amountof time. Suitable adhesions promoters include, but are not limited to,epoxy acrylates, urethane acrylates, carboxylic acid half esters,polyester acrylates, acrylated acrylics and low viscosity monomers.After each intermediate zone has been formed, a spinning process may beused to remove excess chemical solution. As described above with respectto FIGS. 34-42, one or more curing steps may be employed to cure theintermediate zones during the lens manufacturing process.

With further reference to FIGS. 47 and 48, intermediate zones 406, 408are both disposed at an angle that is substantially normal to anteriorsurface 420 and posterior surface 430 of hybrid contact lens 400.According to other embodiments, the intermediate zones are disposed atangles other than 90 degrees with respect to the lens such that atransition is thereby provided. Additionally, intermediate zones 406,408 may include a variety of surface configurations, or geometries, suchas including ledges, protuberances, or projections, serrations,gradations, or any other shape that is not substantially straight, orplanar.

Advantageously, the above-described processes are capable of bonding asoft peripheral portion to a hard central portion comprising a high DKmaterial (i.e., a material having a DK value greater than 30). Such highDK materials include, but are not limited to: fluorosiloxane acrylate;methyl methacrylate; ethyl methacrylate; butylmethacrylate,hexylmethacrylate, ethylene glycol diacrylate; octafluoro pentylmethacrylate, tetramethyldisiloxane, ethylene glycol dimethacrylate,pentafluoro phenylacrylate, 2-(trimethylsiloxyl)ethyl methacrylate,2,2-bis(2-metharyloxyphenyl) propane, N-[2-(N,N-dimethylamino)ethyl]acrylate, 2-(N,N-dimethylamino)ethyl methacryalte,2-(N,N-dimethylamino)propy acrylate, N-vinyl-2-pyrrolidone,N,N-dimthylacrylamide, acrylamide, acrylamine, 2-hydroxyethylmethacrylate, siloxane-ethylene glycol dimethacrylate, trifluoroethylmethacrylate, pentafluorostyrene, pentafluorophenyl methacrylate,pentafluorophenyl acrylate, pentafluoropropyl methacrylate, unsaturatedpolyester; p-vinyl benzylhexafluoroisopropyl ether, siliconylstyrene,siloxanyl alkylmethacrylate, siloxanylalkylamide; flour-siliconeacrylates; silicone-silicone styrene; silicate-silicate acrylate;silicone tetra-acrylate; silicone acrylate; flouro-siloxane acrylate;siloxane acrylate; siloxanylstyrene; siloxanyl alkyl methacrylate; andcombinations thereof.

Suitable materials for the soft peripheral portion include, but are notlimited to: hydroxyethylmethacrylate (HEMA); methyl methacrylate (MMA);Ethyl methacrylate (EMA); butylmethacrylate (BMA), Hexylmethacrylate(HMA), ehtylacrylate (EA), butylacrylate (BA), aminoaklyl containingacrylate or methacrylate; N-vinyl pyrrolidone (NVP); 2-methoxyethylmethacrylate (MEMA); ethylene glycol methacrylate (EGMA);trifluoropropyl methacrylate; pentafluoropentyl methacrylate; N,N-dimethylacrylamide (DMA); acrylamide; methacylamide;tetramethyldisiloxane ethylene glycol dimethacrylate; perfluorophenylmethacrylate; 2-(trimethylsiloxyl)ethyl methacrylate; N-fluoroalkylmethacylamide; bis(2-methacryloxyphenyl) -propane;(N,N-dimethylamino-ethyl)methacrylate; all silicon hydrogels such asCibavision lotrafilcon; all polyHema compounds; and combinationsthereof.

Suitable materials for the intermediate portion include, but are notlimited to: methyl methacrylate; ethyl methacrylate; butyl methacrylate;hexylmethacrylate; T-butylaminoethylmethacrylate;T-Butylaminoethylacrylate; dimethylaminoethyl acrylate; methacrylate, d;fluorinated acrylate; methacrylates including hexafluoro methacryalte,2,2,2-trifluoroethylmethacrylate, 1,1-dihydropropyloctylmethacryalte,hexafluoroisopropyl acryalte and methacrylate, acrylate and methacrylate(mono and di) of perfluorinated ether; silicone containing methacylateincluding 3-methacryloxypentamethyldisiloxane,3-methylacryloxypropyltris (trimethylsiloxy)silane,3-methacryloxypropyltrimethoxysilane, 5-N,N-dimehylacrylamide,N-vinylprolidone, vinyl acetatem 2-ethylhexyl methacrylate, methyl andbutylacrylate and methacrylate; epoxy acrylates; urethane acrylates;carboxylic acid half esters; polyester acrylates; acrylated acrylics;low viscosity oligomers poly(ethylene glycol) acrylate and methacrylate(mono and di); poly(propylene glycol) acrylate and methacrylate (monoand di); diacrylate and dimethyacrylate of polydimethylsiloxanr (M.Wt2000-4000); and combinations thereof.

Astigmatism is a defect of the eye in which rays of light entering theeye fail to meet in a correct focal point after passing through theoptical system, thereby resulting in a blurred and imperfect image. Thedefect is usually the result of a mis-shaped or toric cornea, and thecorrection of astigmatism may be accomplished through the use of a toriccontact lens. According to an aspect of the present invention, for anyof the above-described hybrid contact lens embodiments depicted in FIGS.1-48, the contact lens can be lathed to produce a toric contact lens forthe correction of astigmatism. The shape of a toric lens advantageouslypermits a tear layer to be formed between the lens and the cornea, thusimproving the comfort and health of the eye. The base curve of the highor hyper DK center of the lens preferably is machined to approximate theshape of the lens wearer'cornea such that the radius of curvature of thesoft peripheral skirt is greater than the base curve of the high orhyper DK gas permeable center. The tear layer entrapped between the lensand the cornea serves as a refracting medium having the shape defined bythe base curve, thereby correcting the astigmatic error of themis-shaped cornea below. At the same time, the softer, thinnerperipheral portion of the lens conforms to the cornea and supports theoptical zone in position, resulting in greater comfort for the wearer.Of course, the front curve of the lens can also be selected to correctfor other refractive errors.

One advantage of using a toric lens is that the eyelid force of normalblinking creates a peristaltic-like pump that exchanges the tears underthe lens, contributing to overall comfort, and eliminating dryness, themost frequent complaint of contact lens wearers. Another advantage of isthat the tear layer under a toric lens is comfortable and healthy forthe eye. Moreover, the tear layer has beneficial optical correctionqualities as well. In fact, a tear layer retained behind the base curveof a high or hyper DK gas permeable lens of the present invention maycorrect corneal astigmatism by up to about ten diopters. A furtheradvantage of toric hybrid contact lenses manufactured by the methods ofthe present invention is that they do not require rotationalstabilization. A toric hybrid contact lens constructed according to theprinciples of the present invention may create a superior astigmatismcorrecting capability.

Thus, it is seen that a hybrid hard-soft contact lens system, method,method of manufacture and article of manufacture is provided. Oneskilled in the art will appreciate that the present invention can bepracticed by other than the above-described embodiments, which arepresented in this description for purposes of illustration and not oflimitation. The description and examples set forth in this specificationand associated drawings only set forth preferred embodiment(s) of thepresent invention. The specification and drawings are not intended tolimit the exclusionary scope of this patent document. It is noted thatvarious equivalents for the particular embodiments discussed in thisdescription may practice the invention as well.

1. A hybrid contact lens, comprising: a central zone; a peripheral zone;and an intermediate zone comprising a film.
 2. The hybrid contact lensof claim 1, wherein the film is created around the central zone andcured, thereby forming the intermediate zone.
 3. The hybrid contact lensof claim 1, wherein the film facilitates chemical bonding between thecentral zone and the peripheral zone.
 4. The hybrid contact lens ofclaim 1, wherein the film prevents modification of the physicalcharacteristics of the central zone.
 5. The hybrid contact lens of claim1, wherein the central zone comprises a substantially rigid material andthe peripheral zone comprises a substantially flexible material.
 6. Thehybrid contact lens of claim 1, wherein the intermediate zone is formedat an angle that is substantially normal to the hybrid contact lens. 7.The hybrid contact lens of claim 1, wherein the intermediate zone formsan angled junction between the central and peripheral zones.
 8. Thehybrid contact lens of claim 1, wherein the intermediate zone forms acurvilinear junction between the central and peripheral zones.
 9. Thehybrid contact lens of claim 1, wherein the film is created by soakingthe central zone in a chemical solution for a predetermined amount ofsoaking time.
 10. The hybrid contact lens of claim 9, wherein thechemical solution contains one or more acrylates.
 11. The hybrid contactlens of claim 10, wherein the chemical solution contains methylmethacrylate.
 12. The hybrid contact lens of claim 10, wherein thechemical solution contains ethyl methacrylate.
 13. The hybrid contactlens of claim 10, wherein the chemical solution contains butylmethacrylate.
 14. The hybrid contact lens of claim 10, wherein thechemical solution contains hexylmethacrylate
 15. The hybrid contact lensof claim 1, wherein the central zone comprises a substantially rigid,gas permeable material having a DK of at least
 30. 16. A hybrid contactlens, comprising: a central zone; a peripheral zone; and an intermediatezone comprising one or more acrylates.
 17. The hybrid contact lens ofclaim 16, wherein the intermediate zone contains methyl methacrylate.18. The hybrid contact lens of claim 16, wherein the intermediate zoneis a film that is formed around the central zone, and then cured. 19.The hybrid contact lens of claim 18, wherein the film facilitateschemical bonding between the central zone and the peripheral zone. 20.The hybrid contact lens of claim 18, wherein the film preventsmodification of the physical characteristics of the central zone. 21.The hybrid contact lens of claim 18, wherein the film is created bysoaking the central zone in a chemical solution for a predeterminedamount of soaking time.
 22. The hybrid contact lens of claim 16, whereinthe central zone comprises a substantially rigid material and theperipheral zone comprises a substantially flexible material.
 23. Thehybrid contact lens of claim 16, wherein the intermediate zone is formedat an angle that is substantially normal to the hybrid contact lens. 24.The hybrid contact lens of claim 16, wherein the central zone comprisesa gas permeable material having a DK of at least
 30. 25. The hybridcontact lens of claim 16, wherein the intermediate zone forms acurvilinear junction between the central and peripheral zones.
 26. Ahybrid contact lens, comprising: a substantially rigid center portionhaving a DK value greater than 30; a substantially soft peripheralportion; and an intermediate portion disposed between the substantiallyrigid and soft portions.
 27. The hybrid contact lens of claim 26,wherein the intermediate portion comprises one or more oligomer acrylatemonomers.
 28. The hybrid contact lens of claim 26, wherein theintermediate portion comprises a mixture of methyl methacrylate and anadhesion promoter.
 29. The hybrid contact lens of claim 28, wherein theadhesion promoter is chosen from the group consisting of epoxyacrylates, urethane acrylates, carboxylic acid half esters, polyesteracrylates, acrylated acrylics and low viscosity monomers.
 30. The hybridcontact lens of claim 26, wherein the intermediate portion comprises anadhesion promoter.
 31. The hybrid contact lens of claim 29, wherein theadhesion promoter comprises one or more epoxy acrylates.
 32. The hybridcontact lens of claim 29, wherein the adhesion promoter comprises one ormore urethane acrylates.
 33. The hybrid contact lens of claim 29,wherein the adhesion promoter comprises one or more carboxylic acid halfesters.
 34. The hybrid contact lens of claim 29, wherein the adhesionpromoter comprises one or more polyester acrylates.
 35. The hybridcontact lens of claim 29, wherein the adhesion promoter comprises one ormore acrylated acrylics.
 36. The hybrid contact lens of claim 29,wherein the adhesion promoter comprises one or more low viscositymonomers.
 37. A hybrid contact lens, comprising: a center portioncomprising a first material; a peripheral portion comprising a secondmaterial; and an intermediate portion comprising a third material;wherein each of the first, second and third materials have differentcompositions.
 38. The hybrid contact lens of claim 37, wherein thecenter portion comprises a substantially rigid, gas permeable materialhaving a DK value of at least
 30. 39. The hybrid contact lens of claim38, wherein the substantially rigid, gas permeable material having a DKvalue of at least 30 is chosen from the group consisting of:fluorosiloxane acrylate; methyl methacrylate; ethyl methacrylate;butylmethacrylate, hexylmethacrylate, ethylene glycol diacrylate;octafluoro pentyl methacrylate, tetramethyldisiloxane, ethylene glycoldimethacrylate, pentafluoro phenylacrylate, 2-(trimethylsiloxyl)ethylmethacrylate, 2,2-bis(2-metharyloxyphenyl) propane,N-[2-(N,N-dimethylamino)ethyl] acrylate, 2-(N,N-dimethylamino)ethylmethacryalte, 2-(N,N-dimethylamino)propy acrylate,N-vinyl-2-pyrrolidone, N,N-dimthylacrylamide, acrylamide, acrylamine,2-hydroxyethyl methacrylate, siloxane-ethylene glycol dimethacrylate,trifluoroethyl methacrylate, pentafluorostyrene, pentafluorophenylmethacrylate, pentafluorophenyl acrylate, pentafluoropropylmethacrylate, unsaturated polyester; p-vinyl benzylhexafluoroisopropylether, siliconylstyrene, siloxanyl alkylmethacrylate,siloxanylalkylamide; flour-silicone acrylates; silicone-siliconestyrene; silicate-silicate acrylate; silicone tetra-acrylate; siliconeacrylate; flouro-siloxane acrylate; siloxane acrylate; siloxanylstyrene;siloxanyl alkyl methacrylate; and combinations thereof.
 40. The hybridcontact lens of claim 37, wherein the peripheral portion comprises asubstantially flexible material.
 41. The hybrid contact lens of claim40, wherein the substantially flexible material is chosen from the groupconsisting of: hydroxyethylmethacrylate (HEMA); methyl methacrylate(MMA); Ethyl methacrylate (EMA); butylmethacrylate (BMA),Hexylmethacrylate (HMA), ehtylacrylate (EA), butylacrylate (BA),aminoaklyl containing acrylate or methacrylate; N-vinyl pyrrolidone(NVP); 2-methoxyethyl methacrylate (MEMA); ethylene glycol methacrylate(EGMA); trifluoropropyl methacrylate; pentafluoropentyl methacrylate; N,N-dimethylacrylamide (DMA); acrylamide; methacylamide;tetramethyldisiloxane ethylene glycol dimethacrylate; perfluorophenylmethacrylate; 2-(trimethylsiloxyl)ethyl methacrylate; N-fluoroalkylmethacylamide; bis(2-methacryloxyphenyl) -propane;(N,N-dimethylaminoethyl)methacrylate; all silicon hydrogels such asCibavision lotrafilcon; all polyHema compounds; and combinationsthereof.
 43. The hybrid contact lens of claim 37, wherein the thirdmaterial is a homopolymer.
 44. The hybrid contact lens of claim 40,wherein the homopolymer is MMA.
 45. The hybrid contact lens of claim 37,wherein the third material is chosen from the group consisting of:methyl methacrylate; ethyl methacrylate; butyl methacrylate;hexylmethacrylate; T-butylaminoethylmethacrylate;T-Butylaminoethylacrylate; dimethylaminoethyl acrylate; methacrylate, d;fluorinated acrylate; methacrylates including hexafluoro methacryalte,2,2,2-trifluoroethylmethacrylate, 1,1-dihydropropyloctylmethacryalte,hexafluoroisopropyl acryalte and methacrylate, acrylate and methacrylate(mono and di) of perfluorinated ether; silicone containing methacylateincluding 3-methacryloxypentamethyldisiloxane,3-methylacryloxypropyltris (trimethylsiloxy)silane,3-methacryloxypropyltrimethoxysilane, 5-N,N-dimehylacrylamide,N-vinylprolidone, vinyl acetatem 2-ethylhexyl methacrylate, methyl andbutylacrylate and methacrylate; epoxy acrylates; urethane acrylates;carboxylic acid half esters; polyester acrylates; acrylated acrylics;low viscosity oligomers poly(ethylene glycol) acrylate and methacrylate(mono and di); poly(propylene glycol) acrylate and methacrylate (monoand di); diacrylate and dimethyacrylate of polydimethylsiloxanr (M.Wt2000-4000); and combinations thereof.
 46. A hybrid contact lens,comprising: a central zone; a peripheral zone; and a curvilinearintermediate zone.
 47. The hybrid contact lens of claim 46, wherein theintermediate zone comprises a convex surface that faces the peripheralzone and a concave surface that faces the central zone.
 48. The hybridcontact lens of claim 46, wherein the hybrid contact lens includes atransition area comprising the curvilinear intermediate zone and aportion of the central and peripheral zones.
 49. The hybrid contact lensof claim 48, wherein a radius of curvature of the curvilinearintermediate zone is selected to reduce the amount of peripheral zonematerial within the transition area.
 50. The hybrid contact lens ofclaim 49, wherein the radius of curvature of the curvilinearintermediate zone is selected such that the percentage of peripheralzone material within the transition area preferably is less than about30 percent.
 51. The hybrid contact lens of claim 49, wherein the radiusof curvature of the curvilinear intermediate zone is selected such thatthe percentage of peripheral zone material within the transition areapreferably is less than about 20 percent.
 52. The hybrid contact lens ofclaim 46, wherein the curvilinear intermediate zone improves bondingstrength between the central and peripheral zones, thereby reducing theincidence of lens failure.
 53. The hybrid contact lens of claim 46,wherein the curvilinear intermediate zone is a film.
 54. The hybridcontact lens of claim 53, wherein the film is created around the centralzone and cured, thereby forming the intermediate zone.
 55. The hybridcontact lens of claim 53, wherein the film facilitates chemical bondingbetween the central zone and the peripheral zone.
 56. The hybrid contactlens of claim 53, wherein the film prevents modification of the physicalcharacteristics of the central zone.
 57. The hybrid contact lens ofclaim 53, wherein the film is created by soaking the central zone in achemical solution for a predetermined amount of soaking time.
 58. Thehybrid contact lens of claim 57, wherein the chemical solution containsmethyl methacrylate.
 59. The hybrid contact lens of claim 46, whereinthe central zone comprises a substantially rigid, gas permeable materialhaving a DK of at least
 30. 60. A toric hybrid contact lens forastigmatism fitting, comprising: a central zone; a peripheral zone; andan intermediate zone.
 61. The toric hybrid contact lens of claim 60,wherein the central zone comprises a substantially rigid, gas permeablematerial having a DK of at least
 30. 62. The toric hybrid contact lensof claim 60, wherein the central zone is machined to approximate theshape of a lens wearer'cornea.
 63. The toric hybrid contact lens ofclaim 60, wherein the central zone is machined such that the radius ofcurvature of the peripheral zone is greater than that of the centralzone.
 64. The toric hybrid contact lens of claim 60, wherein the centralzone is dimensioned to correct the astigmatic error of a lenswearer'cornea.
 65. The hybrid contact lens of claim 60, wherein theintermediate zone is a film.
 66. The hybrid contact lens of claim 65,wherein the film is created around the central zone and cured, therebyforming the intermediate zone.
 67. The hybrid contact lens of claim 65,wherein the film is created by soaking the central zone in a chemicalsolution for a predetermined amount of soaking time.
 68. The hybridcontact lens of claim 57, wherein the chemical solution contains one ormore of the following monomers: methyl methacrylate; ethyl methacrylate;butyl methacrylate; hexylmethacrylate; T-butylaminoethylmethacrylate;T-Butylaminoethylacrylate; dimethylaminoethyl acrylate; methacrylate, d;fluorinated acrylate; methacrylates including hexafluoro methacryalte,2,2,2-trifluoroethylmethacrylate, 1,1-dihydropropyloctylmethacryalte,hexafluoroisopropyl acryalte and methacrylate, acrylate and methacrylate(mono and di) of perfluorinated ether; silicone containing methacylateincluding 3-methacryloxypentamethyldisiloxane,3-methylacryloxypropyltris (trimethylsiloxy)silane,3-methacryloxypropyltrimethoxysilane, 5-N,N-dimehylacrylamide,N-vinylprolidone, vinyl acetatem 2-ethylhexyl methacrylate, methyl andbutylacrylate and methacrylate; epoxy acrylates; urethane acrylates;carboxylic acid half esters; polyester acrylates; acrylated acrylics;low viscosity oligomers poly(ethylene glycol) acrylate and methacrylate(mono and di); poly(propylene glycol) acrylate and methacrylate (monoand di); diacrylate and dimethyacrylate of polydimethylsiloxanr (M.Wt2000-4000).
 69. A method of forming a hybrid contact lens, comprisingthe steps of: forming a central zone; forming a protective barrieraround the central zone; and chemically bonding a peripheral zone to thecentral zone.
 70. The method of claim 69, wherein the protective barrierfacilitates subsequent chemical bonding between the central andperipheral zones.
 71. The method of claim 69, wherein the protectivebarrier prevents modification of the physical characteristics of thecentral zone.
 72. The method of claim 69, wherein the central zonecomprises a substantially rigid gas permeable material having a DK valueof at least
 30. 73. The method of claim 69, wherein the peripheral zonecomprises a substantially flexible material.
 74. The method of claim 69,wherein the intermediate zone comprises MMA.
 75. A hybrid contact lens,comprising: a central zone; a first intermediate zone; a secondintermediate zone; and a peripheral zone.
 76. The hybrid contact lens ofclaim 75, wherein the first intermediate zone is a film that is createdaround the central zone and cured.
 77. The hybrid contact lens of claim76, wherein the second intermediate zone is a film that is createdaround the first intermediate zone and cured.
 78. The hybrid contactlens of claim 75, wherein the first and second intermediate zonesfacilitate chemical bonding between the central zone and the peripheralzone.
 79. The hybrid contact lens of claim 75, wherein the first andsecond intermediate zones prevent modification of the physicalcharacteristics of the central zone.
 80. The hybrid contact lens ofclaim 75, wherein the central zone comprises a substantially rigid, gaspermeable material having a DK of at least 30.